Abstract
$Nd_{x}Fe_{77}B_{23-x}(x=4,\;6,\;8,\;11,\;13)$ alloys were prepared by rapid quenching technique. They were crystallized at higher than $650^{\circ}C$ and subsequently the magnetic properties were investigated The melt-spun alloy of x=8 consisted of nearly single metastable compound $Nd_{2}Fe_{23}B_{3}$ and showed the soft magnetic property. In $8{\leq}x{\leq}13$ alloys, the coercivities were increased according to the increase of Nd content but the remanences decreased. In $4{\leq}x{\leq}6$ alloys, the coercivities and the remanences were increased by lowering Nd content. In x=4 alloy, the ratio of soft to hard magnetic phase was 70:30 and the energy product was $96kJ/m^{3}(12MG.Oe)$.
단롤법 급속응고장치를 이용하여 비정질 $Nd_{x}Fe_{77}B_{23-x}(x=4,\;6,\;8,\;11,\;13)$ 합금을 제작하고 $650^{\circ}C$ 이상에서 결정화 시키어 자기적 특성을 조사하였다. 열처리 후의 결정상을 조사한 결 과 x=8 조성에서 준안정상 $Nd_{2}Fe_{23}B_{3}$가 단일상에 가깝게 생성되며 연자기특성을 나타냄 을 알았다. 자기특성 조사결과 $8{\leq}x{\leq}13$ 조성범위에서 Nd 함유량이 증가할수록 보자력은 증가하나 잔류자속밀도는 감소함을 알았다. 그러나, $4{\leq}x{\leq}6$ 합금의 경우 Nd 함유량이 감소할수록 보자 력과 잔류자속밀도가 함께 증가하였다. x=4 합금의 경우 연자성:경자성=70:30의 혼합조직이 얻어지며 $96kJ/m^{3}(12MGOe)$의 높은 에너지적을 나타냈다.