A study on micropipes and the growth morphology in 6H- SiC bulk crystal

6H - SiC bulk 단결정 성장 양상과 micropipe에 관한 연구

Abstract The surface of 6H - SiC bulk crystal grown by sublimation process was investigated by optical microscope observation. Since, in the 6H crystal growing, the crystal had the habitual step growth attitude such that the lateral growth rate along the random a - axis orientation was higher than that along the c - axis of the growth direction, then many steps were developed. There were, also, many micropipes on the surface in the form of as-like large voids. However, they were differenciated with pores and cross- sectional shape of them were close to the circle. In this study, many micropipes, planar defects and the growth steps appeared on the grown crystal surface were investigated.

6H - SiC를 승화법(Sublimation Process)으로 성장하였으며, 성장 결정의 표면에서 나타난 양상에 대하여 광학 현미경을 이용하여 관찰하였다. 6H-SiC는 측면방향(Hexagonal system에서 a축 방향)으로 성장하는 속도가 seed 방향인 c축 방향보다 빠르고, 따라서 많은 성장 step을 관찰할 수 있었다. 또한, SiC 결정의 주된 결함인 micropipe는 성장 후 결정의 표면까지도 형성되고 있어, 거대한 void로 관찰되어졌다. 이것은 pore와는 다르게 구별되며, 완전한 구형의 단면을 가진다. 본 연구에서는 micropipe 및 면결함, 그리고 결정성장시의 step 형성등의 현상에 대하여 광학 현미경으로 조사형 그 결과를 보고하기로 한다.