Preparation and Catalytic Properties of Vanadium-Containing MFI Type Zeolite

바나듐 함유 MFI형 제올라이트의 제조 및 촉매적 특성

  • 김건중 (인하공업전문대학 공업화학과) ;
  • 고완석 (인하공업전문대학 공업화학과) ;
  • 조병린 (인하대학교 화학공학과)
  • Received : 1994.01.17
  • Accepted : 1994.03.03
  • Published : 1994.04.01

Abstract

Vanadium containing MFI type zeolites have been prepared hydrothermally or by the impregnation method with $NH_4VO_3$ solution after dealumination of HZSM-5. Incorporation of vanadium into the framework of zeolite has been demonstrated by XRD, DTA, FT-IR and ESR analyses. Upon $NH_4VO_3$ impregnation and calcination of dealuminated zeolite, vanadium substitution into the framework could be performed like a hydrothermally synthesized zeolite. Vanadium in zeolite is able to pass redox cycles at high temperatures, and it is shown that vanadium is probably fixed and atomically dispersed in the structure of zeolite. The catalytic benzene hydroxylation, hexanes and alcohols oxidation were used for evaluating the properties of vanadium incorporated MFI zeolite.

수열합성법 및 탈알루미늄 처리 이후 $NH_4VO_3$담지법으로 바나듐이 함유된 MFI형 제올라이트를 제조하였다. X선 회절분석, 시차 열분석, 적외선 분광분석 및 전자스핀공명분석을 수행하여 바나듐의 격자구조 내로의 도입을 검토하였다. 탈알루미늄된 ZSM-5에 $NH_4VO_3$를 담지시키고 소성한 경우에도 수열합성법으로 제조한 시료와 같이 바나듐이 구조 내로 도입될 수 있었다. 제올라이트 구조 중의 바나듐은 고온처리에 의해 산화-환원과정을 거칠 수 있으며, 이들은 원자단위로 분산되어 고정됨을 나타내었다. 벤젠 수산화반응과 hexane 및 알코올의 산화반응을 바나듐 함유 MFI형 제올라이트의 특성 검토를 위한 시험반응으로 이용하였다.

Keywords

Acknowledgement

Supported by : 인하학원