Study on Behavior of Cured Rubber Using Stress-Strain Method

응력-변헝 곡선을 이용한 가황고무의 거동에 관한 연구

  • Kim, W.Y. (Dept. of Chemical Tech., Chonbuk Nat'l Dniv.) ;
  • Kim, H.S. (Dept. of Chemical Tech., Chonbuk Nat'l Dniv.) ;
  • Shin, H.C. (Dept. of Chemical Tech., Chonbuk Nat'l Dniv.) ;
  • Hong, S.P. (Pyung Hwa Ind. Co. Ltd.) ;
  • Lee, B.C. (Pyung Hwa Ind. Co. Ltd.)
  • 김완영 (전북대학교 공업화학과) ;
  • 김형순 (전북대학교 공업화학과) ;
  • 신홍철 (전북대학교 공업화학과) ;
  • 홍상표 (평화산업(주) 개발연구소) ;
  • 이범철 (평화산업(주) 개발연구소)
  • Received : 1994.02.18
  • Accepted : 1994.11.24
  • Published : 1994.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

The properties of uncured rubber compound and swelling behavior of cured rubber compound with carbon black(N33O grade) increment. Bound Rubber content(BRC) increased according to carbon black increment and ${\alpha}_f$, behavior of uncured rubber compound filled with carbon black, was 1.46. Carbon black added to rubber compound showed behavior of spherical particle by bound rubber. The $C_1$ values of cured rubber compounds, which measured by the stress-strain method of Mooney-Rivlin, increased with carbon black increment.

본 실험에서는 카본블랙 함량에 따른 미가황고무 혼합물의 물리적 특성과 가황고무 혼합물의 팽윤거동에 대해 고찰하였다. 카본블랙 함량 증가에 따라 미가황고무 혼합물 중의 bound rubber 함량은 증가하였으며 ${\alpha}_f$는 1.46이었다. 또한 고무 혼합물 중의 카본블랙은 구형입자의 거동을 보여주었다. Mooney-Rivlin의 응력-변형 방법에 의해 구한 가황고무의 $C_1$값은 카본블랙 함량 증가에 따라 증가하는 경향을 보였다.