Wear Characteristics of the Extruded Bars of Hypereutectic Al-Si Alloy Powders produced by Rapid Solidification Process

급속응고법으로 제조한 과공정 Al-Si합금분말 압출재의 마멸특성

  • Ahn, Young-Nam (Dept. of Metallurgical Eng., Seoul National Univ.) ;
  • Cho, Gue-Serb (Dept. of Metallurgical Eng., Seoul National Univ.) ;
  • Ra, Hyung-Yong (Dept. of Metallurgical Eng., Seoul national Univ. and RASOM)
  • 안영남 (서울대학교 금속공학과) ;
  • 조규섭 (서울대학교 금속공학과) ;
  • 나형용 (서울대학교 금속공학과 급속응고신소재연구소)
  • Published : 1994.10.31
Download PDF
⟨ Previous Next ⟩

Abstract

Wear resistance and wear mechanism of hypereutectic Al-($15{\sim}40$)wt%Si alloys were investigated. Primary Si particles under $20{\mu}m$ size were formed in hypereutectic Al-Si alloy powders due to rapid solidification. But the Si particles of extruded bars were finely distributed in smaller size than that of atomized powders. The wear mechanism of hypereutectic Al-Si alloys was divided into three types of wear phenomena, which were abrasive wear, delamination wear and severe adhesive wear according to sliding speed and load. At low sliding speed and load, wear mechanism was abrasive wear, so Al-15wt%Si alloy showed the best wear resistance. At high sliding speed and load, wear mechanism was adhesive wear, and Al-40wt%Si alloy showed the best wear resistance.