The purpose of this study is to clarify the influence of the reaction temperature and $AlCl_3$ content on the aluminide coating formation on Ni-based superalloy IN713C in CVD process and to compare its throwing power with that of Pack Cementation process. Aluminide coating was formed by CVD in hot-wall stainless tube reactor from an $AlCl_3-H_2$ mixture in the temperature range $850{\sim}1050^{\circ}C$. At reaction temperature $850^{\circ}C$, the coating thickness and the content of aluminium at the surface were increased as $AlCl_3$ heating temperature was raised. At reaction temperature $1050^{\circ}C$, they were not influenced by the variation of $AlCl_3$ heating temperature. When $AlCl_3$ heating temperature was fixed $125^{\circ}C$, the phases of the coatings were varied from $Ni_2Al_3$ to Al-rich NiAl and to Ni-rich NiAl with the reaction temperature. Therefore, in this study the reaction temperature has been found to be a major factor in determining the phase formed in CVD process. The throwing power of CVD was superior to that of Pack Cementation.