An Experimental Study for Improving the Strength of High Strength Concrete with Silica Fume

실리카흄을 혼합한 고강도콘크리트의 강도향상을 위한 실험적 연구

For complying with the demand of developing high strength concrete, the high strength concrete with higher cement contents and lower water-cement ratio using high range water reducing admixture has been manufactured. In this study, for the purpose of improving the strength of concrete, concrete with silica fume and gypsum was produced so that it was acquired to high compressive strength of $1,058kg/cm^2$, $1,170kg/cm^2$ at age 28 and 91 days, respectively. But neither tensile strength nor modulus of elasticity were highly improved although the compressive strength of the concrete increased. And it was concluded that a higher slump loss of fresh high strength concrete and interior temperature increment of concrete in according to elapsed time than convential concrete should be solved.

콘크리트의 고강도화 요구에 부응하기 위하여 단위시멘트량을 크게 증가시키고 고성능감수제를 사용하여 물-시멘트비를 대폭 감소시킨 고강도콘크리트가 제조되고 있다. 본 연구에서는 콘크리트의 강도를 더욱 향상시키기 위한 목적으로 실리카흄과 석고를 사용하여 콘크리트를 제조하므로써 재령 28 일과 91일의 압축강도가 각각 $1,058kg/cm^2$, $1,170kg/cm^2$되는 고강도를 얻었다. 그러나 인장강도와 탄성계수는 압축강도의 증가에 비하여 크게 향상되지 않았다. 그리고 굳지 않은 고강도콘크리트의 경과시간에 따른 슬럼프 손실과 콘크리트의 내부 온도상승이 기존의 콘크리트보다 큰 점 등이 해결되야 할 문제점이라 생각되었다.