Abstract
The stable defect structure and the single phase region of La$_2O_3$-modified BaTi$O_3$ have been studied by X-ray diffractometer and scanning electron microscope. The stable defect structure of La$_2O_3$-modified BaTi$O_3$ has been identified as [($Ba^x_{Ba})_{1-2x}(La{\cdot}_{Ba})_{2x}][Ti^x_{Ti})_{1-x/2}(V""_{Ti})_{x/2}]O_3$ which consists of La$^{3+}$ ion substitution for Ba$^{3+}$ ion in the lattice structure and the formation of Ti vacancies for the charge compensation. When 3 mol% of La$_2O_3{\cdot}3/2TiO_3$ was added to BaTi$O_3$, the unit cell structure was transformed from tetragonal to cubic and the solubility limit was about 14 mol%. When La$_2O_3{\cdot}3/2TiO_2$ was added above this solubility limit, the second phase, La$_4Ba_2Ti_5O_{18}$, was formed. In the La$_2O_3$-modified BaTi$O_3$, it was found by the liquid phase sintering process that the sinterability was decreased by excess BaO but increased by excess Ti$O_2$.
La$_2O_3$-변형 BaTi$O_3$의 안정한 결함구조와 단일상 영역을 X-선 회절분석기와 주사전자현미경을 사용하여 연구하였다. La$_2O_3$-변형 BaTi$O_3$의 안정한 결함구조는 La$^{3+}$ 이온이 격자구조내의 Ba$^{3+}$ 이온을 치환하고 Ti빈자리가 전하 불균형을 보상하기 위한 결함으로 생성된 [($Ba^x_{Ba})_{1-2x}(La{\cdot}_{Ba})_{2x}][Ti^x_{Ti})_{1-x/2}(V""_{Ti})_{x/2}]O_3$이다. 안정한 결함구조가 형성되도록 BaTi$O_3$에 La$_2O_3{\cdot}3/2TiO_3$를 혼입할 때 단위격자는 약 3 mol%가 혼입될 때부터 정방정에서 입방정으로 변하였고, 고용한계는 약 14 mol%이었다. La2$O_3{\cdot}3/2TiO_2$를 고용한계 이상으로 혼입할 때는 이차상으로 La_4Ba_2Ti_5O){18}$가 생성되었다. La$_2O_3$-변형 BaTi$O_3$ 조성에서 BaO가 과량 존재하면 소결성이 나쁘지만, Ti$O_2$가 과량으로 존재하면 액상소결에 의하여 소결성이 좋아짐을 확인할 수 있다.