Flow and Strength Properties of Cement Mortar mixed with Naphthalene Superplasticizers

나프탈렌계 고성능감수제를 첨가한 시멘트 모르터의 유동성 및 강도특성

In the previous study, naphthalene and /or naphthol were sulfonated wlth sulfuric acid and they were condensated with formaldehyde. The condensates prepared are subjected to the flow and strength tests of cement rnortnr to examine the chemcal effects of cement adrnlxtures. As the results of flow test, the flow of cement mortar mxed wth naphthol condensates(TSC) and naphthol naphthalene cocondensates( NT5) was larger than those mxed with synthetic naphtha lene condensate (NSS). In the experiments of compressive strength after 28 days curing, the hardned cement mortar containing naphthalene naphthol condensates(N1'5) showed a higher compressive strength than those contairung naphthalene condensates(NSS) and naphthol condensates('I'SC). As a results, the synthetic naphthalene condensates(NT5, TSC 1, whlch used i n this study, are greatly expected as good superplasticizers for the concrete.

앞 선 연구에서는 나프탈렌과 나프톨을 혼합 또는 단독으로 술폰화하고 이들을 포름알데히드와 반응시켜 축합물을 합성하였다. 본 연구에서는 이들 축합물의 시멘트 혼화제로서의 성능을 조사하기 위해 시멘트 모르터의 플로우 및 강도 시험을 행하였다. 플로우 시험의 결과, 나프톨 단독 축합물(TSC) 및 나프탈렌 공축합물(NT5)을 첨가한 시멘트 모르터의 플로우 값은 합성 나프탈렌 단독 축합물(NSS)을 첨가한 시멘트 모르텅의 플로우값 보다 큰 값을 나타냈다. 28일 압축 강도 시험에서는 나프탈렌 공축합물(NT5)를 첨가한 경화시멘트 모르터가 나프탈렌(NSS)또는 나프톨 단독 축합물(TSC)을 첨가한 경우보다 약 10% 높은 강도를 나타냈다. 이상의 결과로부터, 본 연구에서 사용한 나프탈렌계 고성능감수제(NT5, TSC)는 콘크리트용의 고성능 감수제로서 크게 기대되어 진다.