bismaleimide취약성을 개선 하기 위하여 toughening agent인 TM120을 첨가하여 carbon/$(\pm 45^\circ)_{2s}$를 제조하고 이들의 파손과 기계적 특성을 인당실험과 음향방출을 통해 자세히 논하였다. 첨가하는 TM120의 비율은 0, 5, 10, 15, 20, 25phr이었고, 1, 4-diazobicyclo-(2, 2, 2)-octane(DABCO) 0.2phr를 경화 촉진제로 사용하였다. 또한, 탄소 섬유는 Toray사의 T300를 사용하였고, 음향방출과 인장실험 결과로 TM120이 적당한 첨가량은 20phr이었으며, TM120은 cabon/$(\pm 45^\circ)_{2s}$의 파손특성과 기계적물성에 많은 영향을 미쳤다.
In detail of fracture and mechanical properties to carbon/BMI$(\pm 45^\circ)_{2s}$ discusses by acoustic emission and tensile testing. The bismaleimide resin from Boots Technochemie Co. was toughened by TM 120 from same Co. The weight proportions of TM 120 were fixed as 0, 5, 10, 15, 20, 25phr. The 0.2phr of 1, 4-diazobicyclo-(2, 2, 2)-octane(DABC0) was used as the accelerator. The used carbon fiber was T300 from Toray Co. The optimum additional proportion of TM120 was proved as 20phr by mechanical testing and at the same time by the results of acoustic emission. toughening agent gives significant influences on the fracture phenomena and mechanical strength.