Abstract
The crystallization behavior and structural change of amorphous $PbTiO_{3}$ precursors prepared by coprecipitation method were investigated by XRD, Raman spectra, TEM, and RDF. The precursors were prepared at $45^{\circ}C$ and pH of 9 from a mixed solution of lead nitrate and titanium tetrachloride derived using $H_2O_2$ or $NH_4NO_3$ as an ion stabilizer. The activation energy and temperature for crystallization of the coprecipitate prepared using $NH_4NO_3$ as an ion stabilizer were lower than that derived from the solution containing $H_2O_2$ stabilizer. The amorphous coprecipitate transformed to transient phase and then to crystalline $PbTiO_{3}$. Average interatomic distances of amorphous states decreased with increasing heat-treatment temperature.
공침법으로 제조된 비정질 $PbTiO_{3}$전구체의 결정화거동과 구조적 변화를 XRD, 라만스펙트럼, TEM, RDF등으로 조사하였다. 전구체는 이온안정제로 $H_2O_2$혹은 $NH_4NO_3$를 사용하여 제조된 질산납과 사염화티탄의 혼합수용액으로부터 $45^{\circ}C$, pH 9에서 제조되었다. 이온안정제로 $H_2O_2$를 사용한 경우보다 $NH_4NO_3$를 사용하여 제조된 공침물이 더 낮은 온도에서 결정화가 시작되며 결정화의 활성화에너지도 더 작은 값을 가진다. 비정질의 공침물은 transient phase를 거쳐 결정 $PbTiO_{3}$로 변태된다. 비정질 상태의 평균 원자거리는 열처리온도의 증가에 따라 감소한다.