Abstract
For the deformation, life time prediction and improvement of the life time in high temperature materials it's very important to know the mechanism of deformation. For these mechanisms the dislocation loop models of Orlova et al. and Mills et al. are used often now. But they show controversial differencies, even if they have unertaken similar experimental tests with the same alloy of A1-5.5at.% Mg. In this work also the similiar tests of them have done under the same temperature of 573 K ; (1) The specimen was deformed by $\sigma$= 30MPa and $\varepsilon$=0.03. (2) Direct after creep deformation of $\sigma$= 30MPa and $\sigma$= 0.03 the stress reduction tests to 15, 10 and OMPa have been performed. (3) To study the loop models dislocation structure and dislocation density ( p ) have been observed.
재료의고온소성변형과 수명예측 및 수명향상을 위하여 재료의 변형기구를 규명하는 것이 매우 중요하다. 이를 위하여 전위환모델이 자주 사용되며, 현재 실험적인 결과를 토대로 한 두개의 중요한 전위환모델로서, Orlova등고 Mills등이 제시한 모델들이 있다. 이들은 모두AI-5.5at.%MG을 사용하였으나 상호 상반된 전위환모델을 설명하고 있다. 그러므로 본 연구에서는 상반된 전위환 모델을 확인하기 위하여 AI-5.5at.%MG을 사용하여 573K의 약 30MPa에서 $\varepsilon$=0.03까지 크\ulcorner시험을 하고, 이러한 크\ulcorner시험후 이어서 각각 약 15,10 및 oMPa의 응력감소 시험도 수행하였으며, 동시에 응력감소 시험 전과 후의 전위구조를 관찰하여 전위환모델을 고찰하였다.