Abstract
Effects of cooling rate, cold reduction %, continuous annealing treatments on the recrystallization texture structure of the A1 killed extra low carbon steel sheet contaning Ti, Nb, and B were investigated. The texture coefficient ratio TC (222)/TC (200) tends to increase with decreasing the cooling rate of the coling process and increasing cold reduction %. However, the texture coefficient ratio tends to decrease as the cold reduction % increases from 80% to 90%, which may be due to the change of the primary texture structure from {554} (225) to {ill] (1 1%). The optimum fabrication procedures for the steel sheet with a maximum texture coefficient ratio may be : furnance cooling after the coiling treatment, 80% cold reduction and the continuous annealing treatment of holding at 80O0C for 1 min., water quenching and then holding at $450^{\circ}C$ for 5min.
Ti, Nb B를 합금원소로 첨가한 알루미늄 킬드 극저탄소 고강도 강판의 재결정 집합조직에 미치는 코일링처리시의 냉각속도, 냉간가공도, 연속어닐링처리등의 효과를 조사하였다. 집합조직계수비 TC(222)/TC(200)는 코일링시의 냉각속도 감소와 냉간압연시의 입하율 증가에 따라 증가하는 경향을 나타내었다. 그러나 압하율이 80%에서 90%로 증가됨에 따라 집합조직계수비가 오히려 감소하는 경향을 나타내는데, 이것은 주집합조직이 {554}<225>로부터 {111}<112>로부터 {111}<112>로 바뀌기 때문인것으로 보여진다. 집합조직계수비를 최대로 만들기위한 최적의 강판제조 공정 조건을 제시하면, 코일링처리시 노냉하고, 냉간압연시의 압하율은 80%로 하며, 연속열처리시 $800^{\circ}C$에서 1분간 유지한다음 $20^{\circ}C$로 수냉하고 다시 $450^{\circ}C$에 5분간 과시효처리하는 것이다.