Physical characteristics of Stocking knitted with Silk/Nylon Compound Yarn

견과 나이론 복합사 스타킹의 품질 특성

This study was carried out to investigate the physical characteristics of stocking knitted with silk/nylon(S/N) compound yarn. In SEM observation, it was found that most part of S/N stocking was well interlaced between silk and nylon yarn. There was no difference between S/N stocking and nylon stocking in shrinkage at warm water and compressive resilience. The suction height and absorbability of S/N stocking was 4~8 times and 3 times higher than that of nylon stocking, respectively. According to the wearing test survey, most of wearers answered that the warmth, the hand and the feeling cool of S/N stocking were better than those of nylon stocking but reversed in elasticity, and they gave sprit opinion on durability responding good impression in total feeling of S/N stocking.

견과 합성 섬유의 단점을 서로 보완하여 새로운 성능을 가지는 신소재를 개발하기 위하여 견사와 나이론사와의 복합사를 제조(이하 S/N 복합사)하고 이들 복합사 스타킹에 대하여 품질을 평가한 결과는 다음과 같다. 1. SEM으로 S/N 복합사로 제편한 스타킹을 관찰한 결과 나이론사는 매끈하게 보이는 반면 견사는 약간 불규칙하게 나타나서 쉽게 판별할 수 있었으며 견사와 나이론사가 서로 잘 포합된 부분과 견사끼리 합쳐진 부분이 발견되었다. 2. S/N 복합사 스타킹의 흡수속도는 나이론 스타킹에 비하여 4~8배 높았고 무연보다 가연할 경우가 높았다. 흡수율에 있어서도 S/N 복합사 스타킹이 나이론 스타킹에 비하여 3배 이상 높았다. 3. 수축율을 보면 상온수에서는 나이론 스타킹과 S/N 스타킹간에 큰 차이는 없었으나 비등수에서는 나이론보다 S/N 스타킹편이 약간 많이 수축되었다. 한편 스타킹간의 수축율과 수축탄성율은 큰 차이는 없었다. 4. S/N 복합사 스타킹의 착용시험 결과 보온성, 촉감은 나이론 스타킹보다 우수하였으나 수축성은 나이론 스타킹에 미치지 못하였다. 그러나 종합적인 호감도는 나이론 스타킹에 비하여 우수한 것으로 나타났다.