Abstract
Hydration process is one of the basic carbonation system. Limestone sludge produced in Pohang Iron & Steel Co., Ltd. We tested for identify of hydration characteristics. The result obtained in this study can be summarized as follows; 1. The classify of limestone sludge is type of ground calcium carbonate(-3mm+325mesh)and the major mineral of calcite, and further more high grade(CaO 51%), fine powder(15~22$\mu\textrm{m}$). 2. Limestone sludge mixed two process sludge, first one is washing process sludge and the other one is wet collect kiln dust. The composition rate is about 8:2. Wet collect kiln dust is major mineral of calcite, too. But the sludge is assumed to one by quick lime, slaked lime and unreacted natural limestone. So, the ideal process is dividing of the washing process sludge and wet collect kiln dust. 3. We manufactured of slaked lime from limestone sludge. To investigate the effect of hydration reactor, the experiments was done with various reactor type as magnetic stirrer, shaking incubator and ultrasonic vibration reactor, respectively. Generally, ultrasonic vibration reactor is excellent hydration for limestone sludge and produced very fine slaked lime powder with ideal distribution. 4. The optimum condition is 10% pulp density, when the manufacture of fine slaked lime powder by ultrasonic vibration reactor. And hydration times to compare the results of the study with ultrasonic vibration reactor of generalized most short time(5~10 min). 5. Finally, the dispersive characteristics of slaked lime powder measured 1~5 $\mu\textrm{m}$ from limestone sludge were compared with those of natural limestone ones(10~20$\mu\textrm{m}$), in order to check applicability of slaked lime with hydration process from limestone sludge.
포항제철소에서 발생되는 석회석슬러지의 기본탄산계 특성중의 일부분인 수화반응 연구를 수행하여 다음과 같은 결과를 얻었다. 1. 석회석슬러지는 광물조성상 calcite이며 고품위(CaO 51%) 미분말(15~22$\mu\textrm{m}$) 석회석으로 보통탄산칼슘 영역 (-3mm + 325mesh)에 속하는 것으로 분류되었다. 2. 석회석슬러지는 수세슬러지와 소성로 습식집진 dust의 혼합슬러지이며 약 8:2의 비율로 구성되어 있다. 수차례 시료채취한 소성로 습식집진 dust는 전형적인 calciteduTdmsk 실조업에서는 일부 열분해 시작한 quick lime과 다시 집진수와 수화된 slaked lime의 혼재가 예상되므로 두 공정 슬러지의 분리로 석회석슬러지의 품위를 향상시킬 수 있다. 3. 석회석슬러지를 소성, 수화하여 제조된 slaked lime의 각종 수화반응기 종류별에 변화에 대해 검토하였다. 일반적인 기계적인 교반기인 magnetic stirrer의 shaking incubator, ultrasonic vibration reactor을 비교 검토한 결과 ultrasonic vibration reactor에서 격렬하지 않은 수화반응과 타반응기 보다 미세한 분체생성 및 균일한 입도분포의 특징을 갖고 있었다. 4. Ultrasonic vibration reactor에서 미분말의 slaked limetod성에 최적인 광액 농도는 10wt%이하였으며, 수화완료 시간도 5~10분으로 타반응기 보다 짧았다. 5. 석회석슬러지는 천연산 석회석을 원료로 한 경우 10~20$\mu\textrm{m}$의 불균질 slaked lime 분체를 생성에 반해 석회석슬러지는 균일한 1~5$\mu\textrm{m}$ 분체를 생성하였다.