The study on the recycle for machined chips and scraps of AZ91 magnesium alloy

AZ91 마그네슘합금 절분 및 스크랩의 재활용에 관한 연구

This paper was focused to optimize hot extrusion condition of Mg machined chips and scraps as fundamental basic research for the recycle of Mg alloy. We have been performed to extrude at $300~380^{\circ}C$ temperature range under the extrusion ratio of 25:1 after cold-pressing AZ91 Mg machined chips and scraps. AZ91 Mg ingots was used as reference materials. Microstructure observation showed that the extruded machined chips were perfectly bonded and extruded materials became fine grain size($20\mu\textrm{m}$) by recrystallization during hot extrusion. The specimens extruded from the machined chips, scraps and Mg ingot indicated tensile strength of 330MPa and the elongation of 10% at room temperature.

AZ91 마그네슘합금 절분 및 스크램외 재활용을 목적으로 절분 및 스크랩을 상온가압하여 빌렛을 얻었다. 이 압출용 벨렛을 압축비율 25:1로 고정하고, 압출온도를 $300~380^{\circ}C$로 변화시켜 가면서 시편을 제조하였으며, 비교재로 마그네슘합금 주조재도 열간압출을 행하였다. 마그네숨합금 절분 및 스크랩을 열간압출함에 따라 매우 미세한 재설정 조직을 얻었으며, 인장강도 및 연산률은 각각 330 MPa, 10%로 주조재를 열간압층한 재료와 거의 비슷한 기계적 특성을 나타내었다.