Abstract
The crystallograpic and magnetic properties of $Eu(Fe_{1-x}In_{x})O_{3}$ (x=0, 0.03과 0.05) have been studied by the methods of X-ray diffraction, $M\"{o}ssbauer$ spectroscopy, and magnetic hysteresis measurement at room temperature. The X-ray results show that the samples have a crystal structure of orthorhombic and unit cell volume of the crystal with the exception of the sample of x=0 increases as increasing the In concentration. In the analysis assuming two sets of six-line of $M\"{o}ssbauer$ spectra, it is found that the magnetic hyperfine field in each of sets decreases increasing x. The linewidth of the absorption lines for the samples increased as increasing x. This implies that the data involve a sum of several hyperfine patterns which have intensity being proportional to $_{n}P_{z}(x)$, the probability of an environment with z such Fe neighbors. The magnetic hysteresis curves show decrease of $M_{s}$ and increase of $H_{c}$ of the samples with increasing x.
$Eu(Fe_{1-x}In_{x})O_{3}$ (x=0, 0.03과 0.05)의 결정구조와 자기적 성질을 상온에서의 X선 회절, $M\"{o}ssbauer$ 분광학 및 자기이력곡선 측정 방법에 의해서 연구하였다. X선 회절 분석 결과는 모든 시료가 orthorhombic 결정구조를 가지며, 단위포의 체적은 x=0을 제외하면 In 농도의 증가에 따라 증가함을 보인다. $M\"{o}ssbauer$ 스펙트럼은 두셋트 여섯 lines을 갖는다는 가정하에 분석하였다. 분석 결과는 각 셋트에서의 초미세 자기장은 x의 증가에 따라 감소하였다. 본 연구의 시료에서 공명 흡수선의 반폭이 x의 증 가에 따라 증가함은, 측정 data가 $Fe^{3+}$ 이온 주위 z개의 $In^{3+}$ 이온이 존재할 확률 분포, $_{n}P_{z}(x)$에 비례하는 초미세 구조에 의한 흡수선의 합으로 이루어졌음을 의미한다. 자기이력 곡선에서 $M_{s}$와 $H_{c}$는 각각 X의 증가에 따라 감소와 증가를 보인다.