Abstract
The Barkhausen noise was measured as the change of line width(39~1.22 mm) and scratching angle($90^{\circ}~50^{\circ}$) with respect of rolling direction in grain-oriented 3 % Si-Fe of 0.30 and 0.27 mm thickness. The two peak phenomena of the noise envelope observed for non-scratching and scratching of line width 39 mm was explained by large activation energy during $180^{\circ}$ domain wall nucleation and annihilation processes. The amplitudes of the noise envelpoes were decreased as the decrement of scratching line width, but did not almost changed below line width of 9.75 mm. It was explained that the decrease in the envelope with increasing scratching number is associated with lower activation energy of $180^{\circ}$ domain nucleation and annihilation in the vicinity of the scratching area. The noise power was decreased as narrower line width. The dependence of the power on the scratching angle was sharpest decreaded at the 50 angle.
두께가 0.30 mm, 0.27 mm인 3% 방향성 규소강판에서 표면 선긋기의 간격(39~1.22 mm)과 집합조직(texture) 방향에 대한 선긋기 각도의 변화($90^{\circ}~50^{\circ}$)에 따라 Barkhausen Noise를 측정하였다. 두께 0.27 mm의 시편에서 선긋기를 하지 않았을 때와 선긋기의 간격이 39 mm인 경우 에 대체로 Barkhausen noise envelope은 두개의 peak 현상을 보였으며, 그 현상은 $180^{\circ}$ 자구벽(domain wall)이 생성과 소멸과정을 거듭할 때 많은 activation energy가 필요함에 따른 것으로 설명할 수 있었다. 선긋기 횟수를 늘려감에 따라 즉 선긋기의 간격이 줄어듦에 따라 Barkhausen noise envelope의 크기값이 감소하였지만, 선간격 9.75 mm부터는 감소현상이 둔화되는 것으로 나타났다. 이는 선긋기 획수가 늘어남에 따라 선긋기 근처에서 $180^{\circ}$ 자구의 생성과 소멸이 쉽게 일어나기 때문에 Barkhausen Noise의 크기가 감소하는 것으로 설명할 수 있다. 이러한 현상은 0.30 mm의 시편에서도 유사하게 설명될 수 있었다. Barkhausen noise power는 선긋기 간격이 줄어듦에 따라 감소하였으며, 각도변화에 따른 결과는 $50^{\circ}$ 근처에서 가장 적은 값을 보였다.
