Abstract
Ferromagnetic resonance experiment was performed to study the variations of micromagnetic structure with heat treatment of melt spun $Fe_{76}Cu_{1}Nb_{3}Si_{14}B_{6}$ alloy for 1h at every $50^{\circ}C$ in the temperature range of $400^{\circ}C-700^{\circ}C$. The variations of micromagnetic structure was discussed qualitatively in terms of the variations of line width ${\Delta}H_{p-p}$ and resonance magnetic field $H_{res}$. With increasing armealing temperature to $400^{\circ}C$, ${\Delta}H_{p-p}$ decreases and $H_{res}$ increases due to the decrease in magnetic anisotropy resulting from structural relaxation during heat treatment. With increasing annealing temperature from 400 to $500^{\circ}C$, ${\Delta}H_{p-p}$ increases and $H_{res}$ decreases due to the increase in magnetic anisotropy resulting from the formation of nanocrystalline particles embedded in an amorphous matrix. With increasing armealing temperature from 500 to $550^{\circ}C$, ${\Delta}H_{p-p}$ decreases and $H_{res}$ increases due to the decrease in magnetic anisotropy resulting from the formation of homogeneous nanocrystalline structure with a minor amorphous phase. Further increase in armealing temperature above $550^{\circ}C$ C causes ${\Delta}H_{p-p}$ to increase and $H_{res}$ to decrease due to the increase in magnetic anisotropy due to the formation of inhomogeneous grain structure and intermetallic compounds.
비정질 $Fe_{76}Cu_{1}Nb_{3}Si_{14}B_{6}$ 합금을 $400\;-\;700^{\circ}C$사이에서 $50^{\circ}C$ 간격으로 1시간 열처리하여 미세자기구조를 알아 보기 위해서 강자성공명 실험을 하였다. 열 처리온도에 따른 미세자기구조 변화를 강자성공명 실험을 통해 얻어진 미분흡수선의 선폭 ${\Delta}H_{p.p}$와 공명자기장의 변화와 관련시켜 정성적으로 고찰한 후 다음을 알 수 있었다. 열처리 온 명자기장은 증가한다. 열처리 온도가 $400^{\circ}C$에서 $500^{\circ}C$로 증가하면 비정질상 내에 미세결정이 불균일하게 나타남으로서 자기이방성 증가하기 때문에, 선폭은 증가하고 공명자기장은 감소한다. 열처리 온도가 $500^{\circ}C$에서 $550^{\circ}C$로 증가하면 균일한 미세결정구조가 형성됨으로서 자기이방성이 감소하기 때문에, 선폭은 감소하고 공명자기장은 증가한다. 열처리 온도가 $550^{\circ}C$이상으로 증가하면 여러가지 결정상들이 혼재한 불균한 조직에 의해 자기이방성이 증가함으로서 선폭은 증가하고 공명자기장은 감소한다.