Manufacture of Pt-transition Metal Alloy Catalyst for PAFC

PAFC용 합금 촉매 제조

  • Kim, Yeong-Woo (Dept. of Ind. Chem., College of Eng., Hanyang Univ.) ;
  • Lee, Ju-Seong (Dept. of Ind. Chem., College of Eng., Hanyang Univ.)
  • 김영우 (한양대학교 공과대학 공업화학과) ;
  • 이주성 (한양대학교 공과대학 공업화학과)
  • Received : 1993.03.10
  • Accepted : 1993.07.07
  • Published : 1993.09.01

Abstract

Corrosivities and catalytic activities of platinum-transition metal alloy catalyses loaded on carbon substrate and were studied by electrochemical method using a unit cell. And the analysis of Pt-alloy catalyst was conducted by x-ray diffractometer. Among the catalysts, the Pt-Mo/carbon, Pt-Fe-Co/carbon and Pt-Fe/carbon catalyst showed more excellent cathodic current densities than others. It was found that most of cathodic current density for the Pt-Mo/carbon electrode was $120mA/cm^2$. The current density of the Pt-Fe-Co/carbon was much higher than that of Pt/carbon, reaching $200mA/cm^2$.

카본 담체에 백금과 전이금속과의 합금 촉매를 제조하여 촉매의 부식성, 촉매능 및 단전지에서의 전극성능을 전기화학적으로 비교 검토하였다. 그리고 합금촉매의 분석은 XRD로 확인하였다. 본 연구에서 제조된 여러 가지 백금 합금 촉매 중 Pt-Mo/carbon, Pt-Fe-Co/carbon 및 Pt-Fe/carbon 촉매가 보다 우수한 산소 환원 전류밀도를 나타내었으나 Pt-Mo/carbon 촉매의 경우 초기 전극전류의 대부분이 촉매의 부식에 의한 전류임을 확인할 수 있었다. Pt/carbon촉매를 사용하였을 경우 나타난 전극의 전류밀도는 $120mA/cm^2$이었으나 Pt-Fe-Co/carbon 의 경우는 $200mA/cm^2$으로 순수 백금촉매보다 우수한 전극성능을 나타내었다.

Keywords

Acknowledgement

Supported by : 동력자원부