EFFECT OF ACID-TREATMENT ON DENTIN BONDING

산 처리가 상아질 접착에 미치는 영향

The purpose of this study was to evaluate the effect of various acid treatments on dentin bonding. Freshly extracted human teeth were uprightly embedded in self curing acrylic resin, and their occlusal surfaces were grinded to expose flat dentin surfaces. The specimens were divided into 4 groups. Specimens of one group were not treated so as to be a control and those of the other three groups were threated with 10% polyacrylic acid, 10% phosphoric acid, and 10-3 solution(10% citric acid/3% ferric chloride) respectively. Primer, bonding resin and composite resin were applied over the treated dentin surfaces sequentially. All specimens were stored in $37^{\circ}C$ distilled water for 24 hours, then the tensile bond strength was measured and the treated dentin surfaces and fracured dentin surfaces were examined under a scanning electron microscope. The results were as follows: Bond strengths of acid-treated groups were higher than those of the untreated group. In the acid-treated groups, bond strength was found to be the highest in the 10-3 solution group followed by the 10% phosphoric acid group and the 10% polyacrylic acid group(P<0.01). On SEM examination of dentin surfaces, the untreated dentin surface showed a remaining smear layer and closed dentinal tubules. Dentin surfaces treated with 10 % polyacrylic acid showed a clean dentin surface without the smear layer, but showed remaining smear plugs in dentinal tubules. A dentin surface treated with 10% phosphoric acid or 10-3 solution showed open dentinal tubules without the smear layer or smear plugs. On SEM observation of the fractured dentin-resin interface, the untreated group showed that failure occurred in the smear layer. The group treated with 10% polyacrylic acid showed no resin tag remained in the dentinal tubules, but resin tags in the dentinal tubules were observed in the group treated with the 10% phosphoric acid or the 10-3 solution. On the failure mode examination, the higher the bond strength of the group, the higher the frequency of cohesive failure. The coefficient between bond strength and cohesive failure rate was 0.71.

산 처리방법에 따른 상아질 접착을 평가하고 표면처리 후의 상아질 표면의 성상변화 및 파단면의 양상을 관찰하기 위해 발거된 구치 에 10% polyacrylic acid (GC Dental Industrial Corp., U. S. A.), 10 % 인산(Bisco Inc., U. S. A.) 및 10-3 용액 (Parkell Bio-Materials, U. S. A.)을 사용하여 상아질 표면을 처리하고 모든 시편에 상아질 접착제인 All Bond 2$^{(R)}$(Bisco Inc., U.S.A.)를 도포하였으며 복합레진 (Silux Plus$^{(R)}$, 3M Co., U.S.A.)을 첨가한 후 접착강도를 측정하고 상아질 표면 및 파단면을 주사 전자현미경으로 관찰, 비교하여 다음과 같은 결과를 얻었다. 1. 접착강도는 상아질 표면을 산 처리한 군이 무처리한 대조군에 비해 높게 나타났고, 산처리를 시행한 군들 간에는 10-3 용액으로 처리한 군이 가장 높았으며 10% 인산으로 처리한 군, 10% polyacrylic acid로 처리한 군의 순이었다(p<0.01). 2. 상아질 표면의 관찰에서, 무 처리의 상아질 면은 상아세관이 개방되지 않은 채 도말층으로 덮혀 있었고, 10% polyacrylic acid로 처리한 상아질 면은 도말충이 제거되고 상아세관이 개방되어 있었으나 상아세관 내에 smear plug이 일부 남아 있었으며, 10% 인산또는 10-3 용액으로 처리한 상아질 면은 도말층 및 smear plug이 모두 제거되고 상아세관이 완전히 개방되어 있음이 관찰되었다. 3. 파단면의 관찰에서, 무 처리군에서는 도말층 내에서 파단이 일어났으며, 10% polyacrylic acid로 처리한 군에서는 상아세관 내 잔존 레진 tag이 관찰되지 않았으나 10% 인산 및 10-3 용액으로 처리한 군에서는 상아세관 내의 잔존 레진 tag이 관찰되었다. 4. 파단 양상에 있어서, 접착강도가 큰 군일수록 응집성 파단의 빈도가 증가되어 나타났으며, 각 시편에서 구한 접착강도와 응집 파단율의 상관 계수는 0.71이었다.