Studies on the Electrochemical Properties of $TiO_{2-x}$ Thin Films Prepared by Air Oxidation and Water Vapor Oxidation

공기 산화와 수증기 산화에 의해 제조된 $TiO_{2-x}$ 박막의 전기화학적 성질에 관한 연구

  • Yong-Kook Choi (Department of Chemistry, Chonnam National University) ;
  • Ki-Hyung Chjo (Department of Chemistry, Chonnam National University) ;
  • Q-Won Choi (Department of Chemistry, Seoul National University) ;
  • Jeong-Sup Seong (Department of Chemistry, Chonnam National University) ;
  • Jeong-Geun Oh (Department of Chemistry, Seonam University)
  • 최용국 (전남대학교 자연과학대학 화학과) ;
  • 조기형 (전남대학교 자연과학대학 화학과) ;
  • 최규원 (서울대학교 자연과학대학 화학과) ;
  • 성정섭 (전남대학교 자연과학대학 화학과) ;
  • 오정근 (서남대학교 화학과)
  • Published : 1993.04.20
Download PDF
⟨ Previous Next ⟩

Abstract

The titanium oxide thin films were prepared by air oxidation and water vapor oxidation. The electrochemical properties of the electrodes were studied in 1M NaOH solution. The peak potentials of oxygen reduction from cyclic voltammogram techniques were observed at aroung -0.9 ∼ -1.0 V vs. SCE and the reaction was totally irreversible process. The electrochemical properties of titanium dioxide electrodes prepared by water vapor oxidation exhibited different from the air oxidized electrodes, but it was similar to single crystal $TiO_2$. The peak potentials of oxygen reduction were observed at slightly more positive than flat band potentials and depended on pH.

티타늄 금속판을 공기산화와 수증기 산화하여 만든 $TiO_{2-x}$ 박막을 전극으로 사용하여 1M NaOH 용액에서 전기화학적 성질을 연구하였다. 순환 전압 전류법에 의한 산소의 환원전위는 SCE에 대해 -0.9 ∼ -1.0 V 근처에서 나타났으며 이들 반응은 전체적으로 비가역적으로 진행되었다. 수증기 산화법에 의해 제조된 $TiO_{2-x}$ 전극들의 전기화학적 성질들은 공기 산화법에 의해 제조된 것과 다르게 나타났으며 900$^{\circ}$이상의 온도에서 제조된 전극들은 단결정 $TiO_2$ 전극들의 전기화학적 성질과 비슷하였다. $TiO_{2-x} $전극에서 산소위 환원전위는 flat band 전위보다 더 양전위 쪽에서 나타났으며 pH 증가에 따라 60mV/pH 정도 감소되었다.

Keywords

References

  1. Nature(London) v.238 A. Fujishima;K. Honda
  2. Bull. Chem. Soc. Jpn. v.48 A. Fujishima;K. Kohayakawa;K. Honda
  3. J. Electrochem. Soc. v.122 A. Fujishima;K. Kohayahawa;K. Honda
  4. Proc. Natl. Acad. Sci. U.S.A. v.72 M. S. Wrighton;D. S. Ginley;P. T. Wolczanski;A. B. Ellis;D. L. Morse;A. Linz
  5. J. Electrochem. Soc. v.122 K. L. Hardee;A. J. Bard
  6. Nature(London) v.257 A. J. Nozik
  7. Mater. Res. Bull. v.10 J. G. Mavroides;D. I. Tchernev;J. A. Kafalas;D. F. Kolesar
  8. J. Am. Chem. Soc. v.98 M. S. Wrighton;A. B. Ellis;P. T. Wolczanski;D. L. Morse
  9. Appl. Phys. Lett. v.28 J. G. Mavroides;J. A. Kafalas;D. F. Kolesar
  10. J. Phys. Chem. v.80 A. B. Ellis;S. W. Kaiser;M. S. Wrighton
  11. J. Electrochem. Soc. v.123 J. H. Kennedy;K. W. Frese
  12. J. Am. Chem. Soc. v.98 M. S. Wrighton;D. L. Morse;A. B. Ellis;D. S. G. Inley;H. B. Abrahamson
  13. J. Chem. Phys. v.32 R. Williams
  14. J. Am. Chem. Soc. v.98 A. B. Ellis;S. W. Kaiser;M. S. Wrighton
  15. Energy Convers v.25 W. W. Anderson;Y. G. Chai
  16. Ber. Bunsenges. Phys. Chem. v.76 R. A. L. Vanden Berghe;W. P. Gomes
  17. Electrochim, Acta v.20 H. Yoneyama;H. Sakamoto;H. Tamura
  18. Appl. Phys. Lett. v.29 A. J. Nozik
  19. J. Appl. Phys. v.47 R. M. Candea;M. Kastner;R. Goodman;N. Hickok
  20. Electrochim. Acta v.27 Y. Matsumoto;T. Shimizu;E. Sato
  21. Int. J. Hydrogen Energy v.8 K. J. Harting;H. Getoff
  22. Chem. Phys. Lett. v.100 D. Miller
  23. Appl. Phys. Lett. v.30 H. Morisaki;M. Hariya;K. Yazawa
  24. Appl. Phys. Lett. v.35 F. Decker;J. F. Juliao;M. Abramovich
  25. Appl. Phys. Lett. v.39 W. T. Kim;C. H. Choe;Q. W. Choi
  26. J. Phys. Chem. v.86 B. H. Chen;J. M. White
  27. J. Phys. Chem. v.90 N. Jaffrezic-Renault;P. Pichat;A. Foissy;R. Mercier
  28. J. Electroanal. Chem. v.237 D. Tafalla;P. Salvador
  29. J. Phys. Chem. v.89 D. Neil Furlong;D. Wells
  30. J. Phys. Chem. v.84 K. Kong;H. Yoneyama;H. Tamura
  31. J. Phys. Chem. v.92 H. Al-Ekabi;N. Serpone
  32. Solar Engineering-1991 J. Pacheco;M. Prairie;L. Yellowhorse
  33. J. Electrochem. Soc. v.124 A. K. Ghosh;H. P. Maruska
  34. J. Electrochem. Soc. v.139 Y. K. Choi;S. S. Seo;K. H. Chjo;Q. W. Choi;S. M. Park
  35. J. Am. Chem. Soc. v.97 S. N. Frank;A. J. Bard
  36. J. Electrochem. Soc. v.125 R. N. Noufi;P. A. Kohl;S. N. Frank;A. J. Bard
  37. Electrochimica Acta v.25 B. Parkinson;F. Decker;J. F. Juliano;M. Abramovich;H. C. Changas
  38. J. Korean Chemical Society v.18 Q. W. Choi;C. H. Choi;K. H. Chjo;Y. K. Choi
  39. Electrochemical Methods A. J. Bard;L. R. Faulkner
  40. J. Electrochem. Soc. v.127 J. F. Juliao;F. Decker;R. Brenzikofer;M. Abramovich
  41. J. Phys. Chem. v.80 J. M. Bolts;M. S. Wrighton
  42. J. Electrochem. Soc. v.128 J. R. Wilson;S. M. Park
  43. CRC Handbook of Chemistry and Physics D. R. Lide(ed.)