Microwave Absorbing Characteristics of Ferrite-silicon carbide surface Films Produced

플라즈마 용사방식에 의해 형성된 페라이트-탄화규소 표면층의 마이크로파 흡수 특성(II)

Plasma spraying method was used to fabricated the microwave absorbing ferrite-silicon carbide on the aluminum-alloy of the fuselage of an aircraft to protect it from RADAR detection. In this paper 15[rm] instead of 34[rm], the mean size of SIC-powder for ferrite-silicon carbide surface films(I) was used. 50(Kg/h) Instead of 70(Kg/h), the powder feed and 100[mm] Instead of 80(mm), spray distance of spray parameters was used. This M/W absorbers were designed experimentally and fabricated trially, as a result of which the relative frequency bandwidth of 2.8% were obtained under the tolerance limits of the reflection coefficients lower than-10[dB], and the maximum absorption thickness becomes 0.5[mm], which is much thinner than that of the conventional ones.

레이다의 추적 및 탐색으로 부터 비행 물체를 보호하기 위한 목적으로, 알루미늄 합금표면에 페라이트-탄화규소 복합물인 마이크로파 흡수층을 플라즈마 용사방식으로 제작하였다. 본 논문에서는 페라이트-탄화규소층(I) 제조시 사용했던 탄화규소 입자의 평균크기인 34[rm]대신에15[rm]가 사용되었으며, 플라즈마 용사변수들 중에서 분말의 공급비율은 70[Kg/h]대신에 50[Kg/h] 그리고, 용사거리는 80[mm[ 대신에 100[mm]가 사용 되었다. X-band(8~12.4(GHz)레이다용 페라이트-탄화규소 전자파 흡수체를 실험적으로 설계하고 시험제작하여 전기적 특성을 평가한 결과, -lOdB의 반사량을 허용한도로 했을 때 약 2.8%의 대역폭이 얻어졌으며, 최대 흡수두께는 0.5(mm)로 매우 양호한 박층형 전자파 흡수체가 얻어졌다.