Abstract
To study the corrosion fatigue begavior of T.M.C.P. steel, the rotary bending fatigue test with the change of concentration of NaCl solution was carried out. Fatigue life in the corrosion environment is decreased markedly in comparision with that in the air. Fatigue limit in the air was about 225 MPa. In case of 3.5% NaCl solution fatigue life could be expressed as .sigma./sub f/=10,392 * (N/sub f/)/sup -o.2923 . According to the paris's rule, crack growth rates could be expressed as da/dN=2.62.*10/sup -7/ .DELTA. K/sup 1.09/(3.5% NaCl solution), da/dN=1.95 *10/sup -7 .DELTA. K/sup 1.05/(1% NaCl solution), da/dN=2.62 * 10/sup -7/.DELTA./sup 0.72/(0.01% NaCl solution) with da/dN expressed in mm/cycle and .DELTA.K in MPa.GAMMA.m. The crack growth rate in the corrosion environment was highest under 3.5% NaCl solution.