Abstract
In this study, magnetite($Fe_3$$O_4$) from the converter dust of the Kwangyang steel making factory has been recove-red by means of the magnetic separation and the sedimentation column. The magnetite recovered from the dust is used for the preparation of Sr-ferrite instead of hematite. The results obtained in this study as follows : 1. The converter EP dust of the Kwangyang steel making factory are composed of $\alpha$-Fe, ($Fe_3$$O_4$) wustite etc. Magnetite in the converter EP dust is recovered by using sedimentation column and plastic bonding magnet. 2. It was confirmed that Sr-ferrite synthesis could be possible without oxidizing roasting of the magnetite. The steps of Sr-ferrite formation are proposed as follows : I$SrCO_3$ $+Fe_3$O$_4$+1/2(1-X)$O_2$longrightarrow$\alpha$ $-Fe _2$$O_3$ $+SrFeO _3$\ulcorner+$CO_2$II. $5.5\alpha$ $-Fe_2$$O_3$ $+SrFeO_3$\ulcornerlongrightarrowSrFe\ulcornerO\ulcorner+1/2(1/2-X)$O_2$3. By using magnetite from the dust insted of hematite, the hard Sr-ferrite magnet of (B.H)\ulcorner=2.64MGOe in the magnetic characteristics was succesfully prepared.
본 연구에서는 광양제철소 전로 dust를 사용하여 자력산별 및 심강(분급) 실험을 통해서 산화철(magnetite)를 분리.회수하였다. 그리고 분리.회수한 산화철(magnetite)과 SrCO$_{#}$를 고상방응시켜 Sr-ferrite를 제조하고 그 자기적 특성은 조사하였으며, 이를 통하여 다음과 같은 결론을 얻었다. 1. 광양제철소 제동전로 Ep dust는 대부분 ${\alpha}$-Fe와 magnetite, wustite 등의 철산화물 상태로 존재하며 자력산별과 심강(분급)실험을 행한 결과 magnetite가 주된 구성물질인 산물을 얻을 수 있었다. 2. 전로 dust 정제를 통하여 얻어진 magnetite와 SrCO$_{4}$를 혼합한 후 하소를 행한 결과 magnetite의 산화배소과정 없이도 Sr-ferrite 생성이 가능함을 확인 하였으며, Sr-ferrite 생성 반응은 다음과 같다. I. $SrCO_3$ $+Fe_3$O$_4$+1/2(1-X)$O_2 $longrightarrow$\alpha$ $-Fe _2$$O_3$ $+SrFeO _3$\ulcorner+$CO_2$ II. $5.5\alpha$ $-Fe_2$$O_3$ $+SrFeO_3$\ulcornerlongrightarrowSrFe\ulcornerO\ulcorner+1/2(1/2-X)$O_2$ 3. 1150$^{\circ}C$에서 1시간동안 하소한 후 1250$^{\circ}C$에서 2시간 동안 산결하여 Br=3.75GK, $_{1}$Hc=1.7KOe, (B.H)$_{max}$=2.64 MGOe인 Sr-ferrite 이방성 영구자석을 제조하였다.