A study on the Magnetic Properties of Co-Cr-Ta Thin Films for Perpendicular Magnetic Recording

수직자기기록용 Co-Cr-Ta 박막의 자기적 성질에 대한 연구

Effects of Ta addition on Co-Cr pependicular magnetic recording media were studied to obtain high perpen-dicular coercivity at lower substrate temperature. For the purpose. magnetic properties and microstructures of Co-Cr-(Ta) films were studied by varying the Cr contents from 17 to 21 at.% and Ta contents for 0 to 3.2 at.%. Effectiveness of Ta addition in increasing perpendicular coercivity was significant for lower Cr content films. The increasement of perpendicular coercivity was more pronounced for the films deposited on $100^{\circ}C$ heated substrate in the case of ${(Co_{83}Cr_{17})}_{98.4}Ta_{1.6}$ composition. The cause of the increase of perpendicular coercivity was considered due to not the grain refinement effects and the improvement of c-axis alignments but increase of Ta and Cr segregation.

Co-Cr계 수직자기기록매체에서 비교적 낮은 기판온도에서 높은 보자력을 얻기위하여 제 3원소로서 Ta의 첨가효과에 대하여 연구하였다. Cr함량이 17-21 at.%로 다른 Co-Cr 계에 Ta함량을 3.2 at.%까지 첨가시켜서 여러조성의 Co-Cr-Ta 박막을 제조하고, 자기적 성질 및 미세구조를 조사하였다. Ta첨가로 인한 수직보자력의 향상효과는 Cr함량이 낮은 박막의 경우에 컸으며, 특히 기판온도가 $100^{\circ}C$인 경우 그 향상효과가 더욱 뚜렷하였다. Ta의 첨가로 인한 수직보자력 향상은 결정립 미세화나, c-축 배향성향상에 의한 것이기 보다는 비강자성원소의 편석이 심화됨에 기인하는 것으로 판단된다.