A Performance characteristics of Pt/C Electrode prepared by Hot Pressing Method

Hot Pressing법에 의해 제조된 Pt/C 전극의 성능특성

Pt loaded porous carbon Pt/C electrode was prepared by hot pressing process to enhance the electrode performance in PAFC (phosphoric acid fuel cell). By changing the hot pressing conditions and PTFE contents, Pt/C electrodes were prepared and the electrochemical characteristics of oxygen reduction and unit-cell performance were evaluated. The optimum condition of hot press to make electrode is 360$^{\circ}C$ and 10 kg/$\textrm{cm}^2$. Maximum performance was obtained at 30 wt% PTFE content in the catalyst layer with 80% utilization of platinum clusters. Unit-cell performance of hot pressed Pt/C electrode was 200 mA/$\textrm{cm}^2$ at 700 ㎷ and stable performance was maintained more than 200 hr.

인산형 연료전지의 전극성능의 향상을 위해 Hot Pressing공정을 사용하여 Pt이 담지된 다공성 탄소전극(Pt/C)을 제조하였다. Hot pressing의 조건, 촉매층에서의 PTEE 함량을 변화시켜 제조한 Pt/C 전극의 전기화학적 산소환원특성 및 인산형 단위전지 성능특성을 비교하였다. 실험결과 Hot Pressing의 최적조건은 36$0^{\circ}C$, 10kg/$\textrm{cm}^2$이었다. 최대성능은 촉매층에 30wt%의 PTFE 함량을 가진 전극에서 얻어졌으며, 이때 백금의 이용율은 80%이었다. 단위전지의 성능측정 결과, hot pressing한 전극의 성능은 700㎷에서 200mA/$\textrm{cm}^2$이었으며 200시간동안 안정적인 성능이 유지되었다.