PECVD of Blanket $TiSi_2$ on Oxide Patterned Wafers

산화막 패턴 웨이퍼 위에 플라즈마 화학증착법을 이용한 균일 $TiSi_2$ 박막형성에 관한 연구

  • Published : 1992.02.01

Abstract

A plasma has been used in a high vaccum, cold wall reactor for low temperature deposition of C54 TiSi2 and for in-situ surface cleaning prior to silicide deposition. SiH4 and TiCl4 were used as the silicon and titanium sources, respectively. The deposited films had low resistivities in the range of 15~25 uohm-cm. The investigation of the experimental variables' effects on the growth of silicide and its concomitant silicon consumption revealed that and were the dominant species for silicide formation and the primary factors in silicon consumption were gas composition ratio and temperature. Increasing silane flow rate from 6 to 9 sccm decreased silicon consumption from 1500 A/min to less than 30 A/min. Furthermore, decreasing the temperature from 650 to $590^{\circ}C$ achieved blanket silicide deposition with no silicon consumption. A kinetic model of silicon consumption is proposed to understand the fundamental mechanism responsible for the dependence of silicon consumption on SiH4 flow rate.

Keywords