Formation of Iron Oxides in a Waste Pickling Liquor

염산 산세 폐액에서의 철산화물의 회수

  • Lee, S. R. (Department of Metallurgical Engineering, Dong-A University) ;
  • Jeong, Y. Y. (Department of Metallurgical Engineering, Dong-A University) ;
  • Ahn, Y. M. (Department of Metallurgical Engineering, Dong-A University) ;
  • Yoon, J. (Kyung-Dong Metal Industry Co. Ltd.) ;
  • Hwang, Y. G. (Department of Metallurgical Engineering, Dong-A University)
  • 이성룡 (동아대학교 공과대학 금속공학과) ;
  • 정유엽 (동아대학교 공과대학 금속공학과) ;
  • 안영민 (동아대학교 공과대학 금속공학과) ;
  • 윤정 (경동금속산업주식회사) ;
  • 황용길 (동아대학교 공과대학 금속공학과)
  • Published : 1992.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

The $\alpha$-FeOOH powders were prepared by allkaline and acidic method on the small scale plant from the waste pickling liquor of iron. $\alpha$-FeOOH, $\alpha-Fe_2O_3$, $Fe_3O_4$ and ${\gamma}-Fe_2O_3$ powders were examined by TEM, SEM, TG-DTA, X-ray diffraction, VSM and chemical analysis. The results obtained from the experiment could be summerized as follows : the reaction time for the preparation of $\alpha$-FeOOH was observed to be smaller in the case of alkaline method and the products was acicular with the size of about $0.5\mu\textrm{m}$. The color of $\alpha-FeOOH and $\alpha-Fe_2O_3$was lovely yellow and red, respectively. The magnetic properties of $Fe_3O_4$ obtained by the reduction of $\alpha-Fe_2O_3$in the $H_2$ atomosphere at $370^{\circ}C$ for 1 hour showed 367(Oe) and 82.7(emu/g).

소규모공장 규모의 알카리 및 산공정법에 의해 철강의 산세 폐액으로부터 $\alpha$-FeOOH를 제조하였으며, 이 때 합성된 분체를 TEM, SEM, TG-DTA, XRD, VSM 및 화학분석으로 물성을 조사하였다. 실험결과에 의하면, $\alpha$-FeOOH의 제조에 있어서 알카리 공정의 반응 시간이 짧으며, 제조된 분체는 약 $0.5\mu\textrm{m}$의 크기로 침상을 나타내었다. 또한 제조 방법에 따라 $\alpha$-FeOOH 와 $\alpha-Fe_2O_3$가 생성되며 이들은 미려한 황색 및 적색을 띠고 있었고 $\alpha-Fe_2O_3$를 $370^{\circ}C$의 수소 분위기에서 1시간 환원하면 367(Oe) 및 86.7 (emu/g)의 자성을 갖는 $Fe_3O_4$ 가 얻어질 수 있었다.