Morphology of Lead Titanate Prepared by Wet Chemical Methods

습식화학법으로 제조된 티탄산 납의 형상

The morphology of lead titanate powders prepared by sol-gel and coprecipitation techniques was investigated as a function of firing temperature and soaking time. PbTiO3 precursor powders were derived from a mixed solution of lead nitrate and titanium tetrachloride at 40℃ to 43℃ and pH of 9.0 to 9.7, and fired at temperatures 350-1000℃ for 1-10h in air. An increase of particle size and agglomeration with increasing calcination temperature and duration could be observed. By annealing sol-gel derived powder at 700℃, the tially-formed acicular(and/or prismatic) primary particles transformed to polyhedral shape with soaking time, and further soaking caused coarsening the polyhedral particles with rounded edges. However, the morphology of the coprecipitated powders was not varied during crystallization.

졸겔 및 공침법으로 제조된 티탄산 납 분말의 형태를 하소온도와 하소시간의 함수로 조사하였다. 질산 납과 사염화 티탄의 혼합용액을 사용하여 40-43℃ 및 9.0-9.7 pH에서 PbTiO3 전구체를 제조하였으며, 350-1000℃에서 1-10시간동안 공기중에서 이들을 히소시켰다. 하소온도와 시간의 증가에 따라 입자의 크기가 증가하고 응집이 심화되었다. 졸겔법으로 제조된 분말을 700℃에서 히소시킬 때, 초기에 형성된 침상형 혹은 각주 형의 입자들은 하소가 진행됨에 따라 다면체형으로 변한뒤, 모서리가 둥근 다면체형 입자로 성장하였다. 공침법으로 제조된 분말은 결정화 과정중에 형태가 변화되지 않았다.