일정응력 및 과대과소응력하에서의 피로크랙 발생전파거동

Fatigue crack behavior under constant stress and periodic overstressing

It is experimented under rotary bending stress that the spacing of two micro hole flaws is adjacent and that it is distant. In order to observe the behavior of fatigue crack propagation, two kinds of specimens are tested under constant stress and periodic overstressing. Although the crack occurs faster when two micro-hole flaws are adjacent than when they are distant, but there is no difference of the number of fracture cycles between two. The crack propagates slower under low-high block stress than under high-constant stress, and it propagates faster under high-low block stress than under low-constant stress. The influence of two-step block stress is serious right after the stress varies.