Abstract
In this study the correlation between material constants and microwave absorbing characteristics of ferroxplana composite microwave absorber used in X-band was investigated. The real part of permeability(${\mu}_{r}'$) was decreased and the imaginary part of permeability(${\mu}_{r}"$) of ferroxplana composite was increased with increaing ferroxplana loading ratio(F/R). The frequency showing maximum attenuation was shifted to lower frequency with increasing absorber thickness. The absorber 2.6 mm thick showed good band width property and 3.2 mm thick showed good attenuation property. From the apphcation of ferroxplana composite's material constants to the region of material constants which satisfy broad band width, it is found that the absorbing characteristics were estimated quantitatively. Estabhshment of material constants' region which satisfies broad band width can make practical application to design of high performance ferrite microwave absorber.
본 연구에서는 복합 ferroxplana 전파흠수체의 X-band에서의 재료정수와 전파흡수특성과의 상관관계를 규명하였다. Ferroxplana 분말과 지지재인 고무와의 함량비(F/R)가 증가함에 따라 ${\mu}_{r}'$은 감소하며, ${\mu}_{r}"$은 증가하였다. 전파흡수체의 두께가 증가함에 따라 최대반사감쇠량이 얻어지는 주파수 가 낮은쪽으로 이동하였으며, 흡수체의 두께가 2.6mm인 경우에는 대역폭이 우수하였고, 두께가 3.2mm인 경우에는 반사감쇠량이 우수하였다. 복합 ferroxplana 전파흡수체의 재료 정수를 광대역화에 요구되는 전파흡수체의 재료정수영역에 적용하여 전파흡수특성을 정량적으로 도출하였으며 이러한 재료 정수영역의 설정은 광대역 ferrite 전파흡수체의 설계지침으로 활용이 가능하다.