A STUDY ON THE BOND STRENGH OF 4-META ACRYLIC RESIN DENTURE BASE TO COBALT-CHROMIUM ALLOYS

4-META의치상레진과 Cobalt-Chromium계 합금의 접착강도에 관한 연구

This study was designed to compre the tensile bond strength of 4-META containging denture base resin to Co-Cr alloys after various surface treatments. Especially the surface treatment of sandblasting the mental with aluminum oxide and treating in oxidizing solution composed of 3% aqueous sulfuric acid with 1% potassium manganate were compared. Effect of surface roughness on bonding was measured after sandblasting with 50um, 300um aluminun oxide and polishing with emery pater. Also the effects of wax and wax solvent on bonding were observed. According to the type of polymerization process, heat-cured Meta-Dent resin and autopolymerizing Meta-Fast resin were used. For some specimnens, the tensile bond strength were measured agter three pre-conditions : 1day after bonding, immersed in water at $75^{\circ}C{\pm}3^{\circ}C$ for 4weeks, under normal ambient condition for 4weeks. The following results were obtained from this study : 1. The bond strengths of resins containing 4-META were significantly higher than those of conventional denture base resins(p<0.05). 2. Autopolymerizing Meta-Fast resin had higher bond strength than heat-cured Meta-Dent, resin(p<0.05). 3. The bond strengths of Biosil and Nobilium to 4-META containging resins were not significally different(p>0.05). 4. Stable adhesion can be achieved when mechanically roughen the metal surface by snadblasting with $50{\mu}m$ aluminum oxide than treating in an oxidizing soluing with potassium manganate(p<0.05). 5. Once the metal surface is contaminated with wax, the bond srtength decreased greatly in spite of wax wash with boiling water. But the bond strength recovered significantly with the use of wax solvent 6. Meta-Dent resin had higher bond strength when roughen the metal surface with $50{\mu}m$ aluminum oxide than with $300{\mu}m$ aluminum oxide(p<0.05). In case of Meta-Fast, resin, the use of $300{\mu}m$aluminum oxide was a little advantageous of bonding, but was statistically insignificant(p>0.05).