Catalytic Properties of Borosilicate in Methanol Conversion

메탄올의 전환반응에서 보로실리케이트의 촉매성질

  • 이계수 (전남대학교 자연과학대학 화학과) ;
  • 조민수 (전남대학교 자연과학대학 화학과) ;
  • 정병구 (전남대학교 자연과학대학 화학과) ;
  • 서곤 (전남대학교 공업화학과)
  • Published : 19900700
Download PDF
⟨ Previous Next ⟩

Abstract

Borosilicate, HZSM-5 zeolite and iron-substituted borosilicate and HZSM-5 zeolite were prepared and their catalytic properties in methanol conversion were studied. The effects of strength and amount of acid site determined from TPD spectra of ammonia on the product distribution was examined. Selectivity to propylene was high over borosilicate with small amount of strong acid site, but selectivity to aromatic compound was high over HZSM-5 zeolite with large amount of the strong acid site. The participation of weak acid site on the conversion did not confirmed, and the product distribution could be explained in terms of the amount of the strong acid site. Although the amount of the weak acid site was increased by substitution of iron, there was no meaningful change in the product distribution.

보로실리케이트와 HZSM-5 제올라이트 및 이들의 골격에 철이 일부 치환된 촉매를 제조하여 메탄올의 전환반응에서 촉매성질을 조사하였다. 산점의 세기와 양이 생성물 분포에 미치는 영향을 암모니아의 승온 탈착곡선으로부터 얻어진 산성도와 연관지어 고찰하였다. 강한 산점이 적은 보로실리케이트 촉매에서는 프로필렌 선택도가 높았으나, 강한 산점이 많은 HZSM-5 제올라이트 촉매에서는 방향족 화합물의 선택도가 높았다. 약한 산점이 전환반응에 기여하는지 여부는 확인되지 않았으나, 생성물 선택도는 강한 산점의 양과 관련지어 설명할 수 있었다. 철의 치환으로 약한 산점이 많아졌으나, 전화율이나 올레핀 선택도에는 영향이 없었다.

Keywords

References

  1. CHEMTECH. v.6 S. L. Meisei;J. P. McCullough;C. H. Lechaler;P. B. Weisz
  2. J. Catal. v.88 M. M. Wu;W. W. Kaeding
  3. ACS Symp. Ser. v.368 N. A. Kutz
  4. Proc. Korea-U.S.A. Catalysis Workshop J. A. Rabo
  5. J. Catal. v.98 T. Inui;H. Matsuda;O. Yamase;H. Nagata;K. Fukuda;T. Ukawa;A. Miyamoto
  6. Proc. 5th Intern. Conf. Mol. Sieves M. Taramasso;G. Perego;B. Notari
  7. Proc. 7th Intern. Zeolite Conf. G. Coudurier;J. C. Vedrine
  8. U. S. Patent, 4, 269, 813 M. R. Klotz
  9. Proc. 7th Intern. Zeolite Conf. R. B. Borade;A. B. Halgeri;T. S. R. Prasada Rao
  10. Catal. Rev. -Sci. Eng. v.25 C. D. Chang
  11. Appl. Catal. v.27 W. G. B. Mandersloot;C. P. Nicolaides;M. S. Scurrell
  12. J. Catal. v.70 N. Y. Topsoe;K. Pederson;E. G. Derouane
  13. Catalysis on the Energy Scene Z. Gabelica;G. Debras;J. B. Nagy;S. Kaliaguine(ed.);A. Mahay(ed.)
  14. U. S. Patent, 3,702, 886 R. J. Argauer;G. R. Landolt
  15. ACS Symp. Ser. v.248 Z. Gabelica;E. G. Derouane;N. Blom
  16. U. S. Patent, 4, 285, 919 M. R. Klotz;S. R. Ely
  17. J. Catal. v.101 H. Kitagawa;Y. Sendoda;Y. Ono
  18. J. Phy. Chem. v.90 J. M. Thomas;X. S. Liu
  19. J. Catal. v.93 C. T. -W. Chu;G. H. Kuehl;R. M. Lago;C. D. Chang
  20. U. S. Patent, 4, 268, 420 M. R. Klotz
  21. Structure and Reactivity of Modified Zeolite T. Inui;T. Suzuki;M. Inoue;Y. Murakami;Y. Takagami;P. A. Jacobs(et al. Ed.)
  22. U. S. Patent, 3, 972, 832 S. A. Butter;W. W. Kaeding
  23. J. Catal. v.86 C. D. Chang;C. T. -W. Chu;R. F. Socha
  24. Proc. 6th Intern. Zeolite Conf. T. Inui;H. Matsuda;Y. Takagami
  25. J. Catal. v.73 J. C. Vedrine;A. Auroux;P. Dejaifve;V. Ducarme;H. Hoser;S. Zhou
  26. J. Catal. v.61 W. W. Kaeding;S. A. Butter
  27. CHEMTECH. v.17 C. D. Chang;A. J. Silvestri
  28. J. Chem. Soc. Japan H. Okado;H. Shoju;K. Kawamara;Y. Kohtaku;Y. Yamazaki;T. Sano;H. Takaya
  29. 화학공학 v.26 서곤;송요순;변대홍;하백현
  30. J. Catal. v.99 R. M. Dessau
  31. J. Catal. v.47 C. D. Chang;A. J. Silvestri
  32. J. Catal. v.78 R. M. Dessau;R. B. Lapierre
  33. Catal. Rev. -Sci. Eng. v.26 C. D. Chang