Characteristics of Reoxidized-Nitrided-Oxide Films Prepared by Sequential Rapid Thermal Oxidation and Nitridation

연속적 급속열처리법에 의한 재산화질화산화막의 특성

Oxide (RTO), nitrided-oxide(NO), and reoxidized-nitrided-oxide(ONO) films were formed by sequential rapid thermal processing. The film composition was investigated by Auger electron spectroscopy(AES). The Si/SiO2 interface and SiO2 surface are nitrided more preferentially than SiO2 bulk. When the NO is reoxidized, [N](atomic concentration of N) in the NO film decreased` especially, the decrease of [N] at the surface is considerable. The weaker the nitridation condition is, the larger the increase of thickness is as the reoxidation proceeds. The elelctrical characteristics of RTO, NO, and ONO films were evaluated by 1-V, high frequency (1 MHz) C-V, and high frequency C-V after constant current stress. The ONO film-which has 8 nm thick initial oxide, nitrided in NH3 at 950\ulcorner for 60 s, reoxidized in O2 at 1100\ulcorner for 60 s-shows good electrical characteristics such as higher electrical breakdown voltage and less variation of flat band voltage under high electric field than RTO, and NO films.