A STUDY ON THE ANODIC POLARIZATION OF DENTAL AMALGAMS

수종 아말감의 Anodic Polarization에 관한 연구

The purpose of this study was to observe the anodic polarization curve from 4 kinds of low copper amalgam (Fine cut alloy, Spheralloy, Aristalloy and Amalcap) and 4 kinds of high copper amalgam (Dispersalloy, Sybraloy Orosphere and Tytin) obtained by using the potentiostat. The specimen made as the direction of manufacturer was stored at room temperature for about 7 days. The standard surface preparation was routinely carried out. The 0.9% saline solution was used as electrolyte in pH 6.8-7.0 at $37^{\circ}C$. The open circuit potential was determined after 30 minutes' immersion of specimen. The scan rate was 1mV/sec and the surface area of amalgam exposed to the solution was 0.785$cm^2$ for each specimen. All potentials reported are with respect to Ag/AgCl eelctrode. The following results were obtained. 1. The corrosion potential of high copper amalgams was higher than one of low copper amalgams, and the current density of high copper amalgam was lower than one of low copper amalgams. 2. The low copper amalgams had the similar pattern of polarization curve, but the high copper amalgams had the different pattern one another. 3. The polarization curve of Orosphere amalgam which is the admixed type was similar to one of low copper amalgam.