The Microstructural Changes of Free-Annealed Nylon 6 Filament Yarns - Comparison of UDY, POY, and FDY -

무긴장 열처리 나일론 6 필라멘트사의 내부구조 변화 - 미연신사, 부분배향사 및 완전연신사의 비교 -

The microstructural changes of nylon 6 UDY, POY and FDY were compared after free-annealing through crystallinity, birefringence, and melting behavior analyses. Free-annealing was done at various temperatures $(120^{\circ}C\;,140^{\circ}C,\;160^{\circ}C,\;180^{\circ}C,\;200^{\circ}C)$ and times (15 min., 30 min., 60 min.) using vaccum oven. Crystallinity was measured by the density gradient column technique and birefringence was measured using a Nikon polarizing microscope with a quartz wedge and Senarmont compensator. Melting behavior was investigated on the basis of DSC melting corves. Crystallinites of specimens increased as the treatment temperature and time increased. Birefringence of UDY increased after annealing and increased as the treatment temperature increased. On the other hand, those of POY and FDY decreased after annealing. Especially, the changes of crystallinity and birefringence of treated POY were particularly lower than those of treated UDY and FDY. Melting peaks of untreated UDY, POY and FDY were different in the position and the shape, but little change was seen in melting peaks in spite of increasing the annealing temperature and time. UDY and FDY showed single melting peaks in all the specimens. But POY showed double melting peaks, which means the coexistences of crystals with different thermal properties.