A Fundamental Study on the Fatigue Behavior in the Joints of Steel Members

강부재(鋼部材) 이음부(部)의 피로거동(疲勞擧動)에 관(關)한 기초적(基礎的) 연구(硏究)

  • 이용재 (강원대학교 대학원 토목공학과) ;
  • 정영화 (강원대학교 공과대학 토목공학과)
  • Published : 1989.10.31

Abstract

For the study of the fatigue behavior, high-strength bolted connections on a small scale were manufactured, and carried on fatigue tests. Its experimental values were analysed by stress-fatigue life (S-N) curve. Three types of specimens : the base metal, the cireular hole and the welded sperimens had same net section were made. Through the same tests those experimental values were compared with those of the high-strength bolted conneetions. The results of these studies are as followings. It was found that the fatigue strength in $F_{n=100,000}$ and $F_{n=2,000,000}$ of the high-strength bolted conneetions were much more about 14% and 16% than that of the base metal specimen. It was thought that this trend was due to frictional force increasing fatigue strength. It was known that fatigue strength in $F_{n=100,000}$ and $F_{n=2,000,000}$ of the welded joints were less 29% and 21% than that of base metal specimen. It was thought that that trend was due to weld flaw. It was appeared that the fatigue strength in $F_{n=100,000}$ and $F_{n=2,000,000}$ of the high-strength bolted connections were much more about 38% and 30% than that of welded joint. It was thought that it was due to both frictional force increasing the fatigue strength in bolted connections and weld flaw decreasing the fatigue strength in welded connections. It was found that the fatigue strength in $F_{n=100,000}$ and $F_{n=2,000,000}$ of the B3 specimens were much more 2% and -2% than that of the B4 specimen. It was thought that that trend was due to the frictional force, which concerned with shape of specimen. It was known that the fatigue strength in $F_{n=100,000}$ and $F_{n=2,000,000}$ of the specimen with circular hole was less 61% and 65% than that of base metal. It was known that the allowable stress for bolted joint was higher than that of welded Joints. If that research is continued and more data are accumulated it can be expected that a basic pattern to provided the indicator of the fatigue design of the bolted connections of steel structures and persume the safety and lifeproof of existing structures is given.

Keywords