Oxygen Index of Fire-Retardant-Treated Plywood in Burning Test

산소지수법(酸素指數法)에 의한 내화처리합판(耐火處理合板)의 연소시험(燃燒試驗)

To obtain relative effectiveness in fire resistance among fire retardant chemicals, oxygen indices were determined for 3.5 mm thick, three-ply, meranti plywoods, treated with 5 commercial chemicals and water and then press-dried, through Up and Down method following oxygen index test of ASTM D 2863-77. The oxygen indices obtained were 28.4 for ammonium sulfate, 26.9 for monoammonium phosphate, 43.4 for diammonium phosphate, 30.1 for borax-boric acid, 32.4 for minalith, and 25.5 for water. Therefore, diammonium phosphate was found to rank first in fire-retardant effectiveness, followed by minalith, borax-boric acid, ammonium sulfate, and monoammonium phosphate in turn, judging from the fact that highly flammable materials are likely to have a low oxygen index.

내화제간(耐火劑間)의 상대적(相對的)인 내화효과(耐火效果)를 비교(比較), 검토(檢討)하여 보기 위하여 메란티(meranti) 합판(合板)에 5종(種)의 내화제(耐火劑)와 수처리(水處理)를 하고 열판건조(熱板乾燥)시킨 다음, ASTM D 2863-77의 산소지수법(酸素指數法)에 의거하여 Up and Down법(法)을 통하여 각각의 산소지수(酸素指數)를 구하였다. 시험결과(試驗結果)에 의하면 황산(黃酸)암모늄이 28.4, 제(第)1인산(燐酸)암모늄이 26.7, 제(第)2인산(燐酸)암모늄이 43.4, 붕사(硼砂)-붕산(硼酸)이 30.1, 미날리스가 32.4, 그리고 수처리(水處理)가 25.5의 산소지수(酸素指數)를 나타냈는데, 연소성(燃燒性)이 큰 물질(物質)일수록 낮은 산소지수(散素指數)를 지닌다는 사실(事實)로 미루어 볼 때 내화제간(耐火劑間)의 내화효과(耐火效果)는 제(第)2인산(燐酸)암모늄, 미날리스, 붕사(硼砂)-붕산(硼酸), 황산(黃酸)암모늄, 제(第)1인산(燐酸)암모늄의 순(順)으로 크다는 것을 구명할 수 있었다.