Isolation and Analysis of Micro-Regions Having Possibly Higher Tc in Oxide Superconductors

산화물계 초전도체의 고변이 송도부근의 곡출과 이의 성분 분석에 관한 연구

In conclusion, a high-Tc superconducting YBa sub(2) Cu sub(3) O sub(y) phase with zero resistance at about 90K was successfully prepared by nitrate solution method with densed micro structure. The result of the EDAX analysis on the isolated particles using the microscopic meissner effect showed that the particles were isolated at higher temperature due to the differences in O vacances rather than the differences in chemical compositions. The composition of the isolated particles were almost identical to the starting compositions on the samples prepared by the solid reaction and nitrate solution method but the Ba-rich composition were seen in the coprecipitated sample. The isolation process on Bi system was not successful due to the weak dimagnetism even though its high Tc above the liquid nitrogen temperature.

산화물 초전도체에 있어서 고천이 임계온도를 갖는 미소영역을 추출하여 이를 분석하기 위하여 La-Ba-Cu-O 계, Y-Ba-Cu-O 계 및 Bi-Pb-Sr-Ca-Cu-O 계의 초전도체를 고상법 및 nitrate solution method로 제조하였다. 제조된 시료들에 대해서 x선회절분석과 저항을 측정하였다. 이들 시료 중에서 고천이온도를 나타내는 미소부분을 Meissner효과를 이용한 추출법으로 분리 해내고 EDAX로 이를 분석하였으며, 이들 결과를 요약하면 다음과 같다. nitrate solution method를 적용하면 YBCO계에 있어서 비교적 단시간에 치밀한 미세조직을 갖는 천이 온도 90K의 초전도체를 제조할 수 있다. Meissner효과를 이용하여 고천이온도에서 추출해낸 미소영역의 EDAX분석 결과는 고상법을 사용한 YBCO-23S와 nitrate solution method으로 제조한 YBCO-23N 및 YBCO-36N 에서는 초기의 조성과 거의 같았으며, 고천이 온도에서 추출된 미소영역은 조성보다는 산소 결함의 차이에 기인한 것으로 생각된다. 공침법으로 제조한 YBCO-23NA 에서는 과도한 Ba의 조성을 보였으며, 천이온도 100K 인 Bi계에서는 약한 반자성효과 때문에 추출이 불가능하였다.