Weldability of boron containing low carbon quenched and tempered 60kg/mm$^{2}$ steel with low cold cracking susceptibility

저탄소 B 첨가 60kg/mm$^{2}$급 저균열감수성 조질고강력강의 용접성

  • 장웅성 (산업과학기술연구소 용접연구센타) ;
  • 김태웅 (산업과학기술연구소 용접연구센타) ;
  • 장래웅 (산업과학기술연구소 용접연구센타) ;
  • 엄기원 (한양대학교 정밀기계공학과)
  • Published : 1989.03.01

Abstract

The weldability and joint performance were evaluated for newly developed 60kg/mm$\^$2/ steel which had low cold cracking susceptibility. The main results obtained were as follows; In case of quenched and tempered 60kg/mm$\^$2/ steels, it was very effective to improve weldability and joint performance by lowering carbon and Pcm level. Very small addition of about 0.001 to 0.002wt% boron exhibited an appreciable compensation effect on strength which was decreased by lowering carbon and Pcm level. As a result, the newly developed steel was able to be welded without preheating and exhibited superior joint performance to conventional steels.