Suitable Conditions of Producing the LVL from Pitch Pine and its Paint Film Durability

리기다소나무 단판적층재(單板積層材)의 제조조건(製造條件)에 따른 물리적성질(物理的性質) 및 도장성능(塗裝性能)

This study was carried out to investigate the physical and mechanical properties. durability of adhesive bond and paint film for the basic data which were required to determine the suitability as a raw material for furniture the laminated veneer lumber (LVL) with pitch pine (Pinus rigida Mill). The results obtained were as follows; 1) The proper pressing time for making the LVL was over 45 second per milimeter of LVL thickness. 2) The bending strength of the LVL was lower than that of the solid wood but the compressive strength of the LVL was similar to that of the solid wood. The strength increased with the decrease of veneer thickness. 3) The impact bending absorbed energy of the LVL was 0 to 0.3 kg.m/$cm^2$ in the direction of parallel to the grain. The energy of the LVL was lower than that of the solid wood (0.68 kg.m/$cm^2$). 4) In warm water soaking and cold-dry tests, delamination of adhered layers surface crack, swelling, and color change were not found when the hot pressing time was over 45 second per milimeter of LVL thickness. As a result of soak under vacuum test shrinkage in the direction of parallel to the grain was about -1.0 percent and. was about 3.0 percent in the direction of the perpendicular to the grain. 6) The film cacks on the LVL's surface after the wet and cold-dry test were not found at all. 7) In the use of the LVL for interior decoration it was considered that the surface of the LVL be overlaid crossly with fancy veneers of birch and paulownia, etc. This cross overlayirg methods have resulted in few cracks on the fancy veneer.

리기다소나무 단판적층재(單板積層材)(LVL)의 가구용재(家具用材)로서의 적합성(適合成) 여부(與否)를 판단(判斷)하기 위한 기초자료(基礎資料)를 제공(提供)하고자 요소 멜라민수지(樹脂)와 페놀수지접착제(樹脂接着劑)를 사용(使用)하여 단판적층재(單板積層材)를 제조(製造), 그 물리적(物理的), 기계적(機械的) 성질(性質), 접착내구성(接着耐久性) 및 제조성능(製造性能)을 검토(檢討)한 결과(結果)는 다음과 같다. 1. 리기다소나무 LVL 제조(製造)를 위한 적정압체시간(適正壓締時間)은 단판(單板)두께 1mm당(當) 45초(秒) 이상이 요구(要求)되었다. 2. 휨강도(强度)는 소재(素材)에 비(比)해 낮았으나 압축강도(壓縮强度)는 비슷하였고 단판(單板)의 두께가 얇을수록 강도(强度)는 증가(增加)하는 경향(傾向)이였다. 3. 충격(衝擊)휨흡수(吸收)에너지는 두께 2.5cm의 경우(境遇) 섬유직각방향(纖維直角方向)(상(上))이 $0.03kg{\cdot}m/cm^2$, 섬유방향(纖維方向)이 $0.24kg{\cdot}m/cm^2$으로 $0.68kg{\cdot}m/cm^2$인 소재(素材)에 비(比)해 매우 낮았다. 4. 열압체시간(熱壓締時間)을 45초(秒)/mm 이상(以上)으로 하면 침지박리(浸漬剝離) 및 한열반복시험시(寒熱反復試驗時), 접착층(接着層)의 박리(剝離), 표면할열(表面割裂), 부풀음, 변색(變色) 등(等)이 발생(發生)하지 않았다. 5. 진공침수시험(眞空侵水試驗)은 결과(結果), 섬유방향(纖維方向)으로서 수축율(收縮率)은 약(約) 1.0%, 섬유직각방향(纖維直角方向)(횡방향(橫方向))은 약(約) 3%였으며, 1~4개(個) 정도(程度)의 표면할제(表面割裂)이 관찰(觀察)되었다. 6. 온냉건고시험(溫冷乾燥試驗)에 의한 리기다소나무 LVL의 도막할열(塗膜割裂)은 전혀 관찰(觀察)되지 않았다. 7. 리기다소나무 LVL을 내장용(內粧用)으로 사용(使用)할 경우(境遇), 부착용화장단판(付着用化粧單板)으로서는 단판자체(單板自體)의 할열(割裂)이 적은 단판(單板)을 사용(使用)하여야 하며 부착용화장단판(付着用化粧單板)과 LVL의 표면(表面)이 서로 직교(直交)되도록 접착(接着)해야 표면할열(表面割裂)의 발생(發生)이 적고 표면부착성(表面付着性)이 향상(向上)되었다. 결론적(結論的)으로 리기다소나무 LVL은 접착성(接着性)은 매우 양호(良好)하였으며 휨강도(强度), 압축강도(壓縮强度) 및 충격(衝擊)휨흡수(吸收)에너지 등(等)은 가구재료(家具材料)로써 적정수준(適正水準)이었으나 단판자체(單板自體)의 옹이 및 할열(割裂)로 인(因)해 가구재료(家具材料)로 사용(使用)할 경우(境遇), 품질(品質)이 좋은 단판(單板) 즉, 화장단판(化粧單板) 등(等)으로 표면(表面)해양 할 것으로 생각되었다.