Matrix Development in Cast Iron by Addition of Mischmetal Hydrides

주철(鑄鐵)의 기지조직(基地組織)에 미치는 Mischmetal Hydride의 첨가효과(添加效果)

In this study we have investigated the effects of Mm, MmH and $MmH_2$ on the matrix development in cast iron, The conclusive summary is as follows: The spheroidal graphite was observed when 0.5wt.% or more of mischmetal was added and the matrix was of ledeburite structure, but bull's eye structure was not observed. On the other hand, the bull's eye structure was observed when 0.25wt.% of MmH, or 0.25wt.% to 0.5wt.% of $MmH_2$ was added. Above limit of the additives, the matrix changed into ledeburite structure. As the hydrogen content of mischmetal compound increased from MmH, the range of additives to obtain bull's eye structure expanded. This reveals the significant effect of mischmetal hydride on matrix development in cast iron and the possibility of practical use of the additives.