Studies on the Dimensional Stabilization of Wood -Especially by the Solution of Different Composition by PEG Molecular Weight-

목재(木材)의 치수 안정화(安定化)에 관(關)한 연구(硏究) -Polyethylene Glycol의 혼합액(混合液)을 중심(中心)으로-

This study was carried out to elucidate the desirable PEG molecular weight and it's blending methods which can promote the dimensional stabilization of Corpus controversa, Quercus variabilis and Prunus sargentii. The results may be summarized as follows: 1. PEG polymer loading in woods was affected by specific gravity of wood. And the PEG polymer loading was satisfactory except in Quercus variabilis, which shows the blending method of PEG V was proper. 2. Bulking coefficiency of PEG V was high in Corpus controversa and Prunus sargentii, and it is necessary to paint or coat water-proofing wood preservative: for high bulking coefficiency of Quercus variabilis. 3. In the treatment of PEG V, the antishrink efficiency of Prunus sargentii was 82.59% and that of Quercus variabilis 62.79%. 4. Dimensional stabilization of hardwoods did not have apparant relation with PEG blending method. 5. Judging from results, PEG-400 and PEG-1000 would be enough for dimensional stabilization of hardwood having high specific gravity if other factors are considered well.

본 연구는 활엽수재(闊葉樹材)인 층층나무(Cornus Controversa Hemsl), 굴참나무(Quercus variabilis Blume) 및 산벚나무(Prunus sargentii Redher)를 시험편(試驗片)으로 하여 치수안정화효과(安定化效果)를 높일 수 있는 PEG 적정분자량(分子量)과 혼합방법(混合方法)을 혼합비 I, II, III, IV 및 V 중에서 찾는데 그 목적이 있었으며 실험결과는 다음과 같았다. 1. 목재내(木材內) PEG 주입율(注入率)은 비중에 따른 영향을 받았으며 굴참나무를 제외하고 만족할만한 주입율을 나타내어 적정혼합방법은 PEG V임을 알았다. 2. PEG V용액에서의 팽윤효과(澎潤效果)는 층층나무, 산벚나무에서 높았으며, 굴참나무의 팽윤효과(澎潤效果)를 높이기 위해서는 방수성약제(防水性藥劑)의 도장(塗裝)이 필요하다. 3. PEG V용액에서 산벚나무가 82.59%로 가장 높은 항수축능(抗收縮能)을 보였고 굴참나무가 62.79%로 가장 낮은 값을 보여 주었다. 4. 활엽수재(闊葉樹材)의 치수안정화(安定化)는 PEG의 혼합방법에 따라 커다란 차이를 나타내지 않았다. 5. 이상과 같은 실험결과를 종합 분석한 결과 비중이 높은 활엽수재(闊葉樹材)의 경우에는 PEG-400과 PEG-1000으로 혼합하되 외부인자를 충분히 고려할 필요가 있다.