Studies on Methacrylate Finish with Silk Fabrics and their Anticrease

Methacrylate 견직물가공과 방추도개선에 대한 연구

These studies are carried out to improve silk availability for anticrease by useing methacrylate monomer polymerization method with in silk fiber. For this purpose, degree of anticrease, stiffness and shrinkage of various silk fabrics, included finish or not, after repeat of washings and polyster fabric was compared as standard. The adopted samples are ; 1. Polyester, Georgette, Woven density…90cm-85g/m 2. Silk, Twill, Degumed, Light, Woven density…90cm-90g/m 3. Silk, Twill, Degumed, Heavy, Woven density…90cm-200g/m 4. Silk, Stain, Degumed, Light, Woven density…90cm-90g/m The reached results are as followings. 1. The results of improving on anticrease by the finished method were about ten per cent increase against their original samples. 2. The light density silks showed satisfactory improve for anticrease, but the heavy one remained as rather poor condition. 3. The results for degree of textile stiffness were investigated to make sure reserve their textile feeling and observed to be good condition upon the finish work. 4. Textile shrinkage after the repeat of soap wash was investigated on indivisual test sample and silk fabrics showed more shrinkage than polyester which it seemed to be tentering shrinkage druning their general finishing processes. 5. The investigation showed that anticrease, stiffness and shrinkage of the sample textile were more or less deteriorated regardless silk or polyester by the repeat of washings. These matters are considered that such results were obtained because of the fiber fatigue nature. 6. The report reached that silk textiles should be used by dry cleaning methed after finish of any resin finish to reserve their improved anticrease nature.

본 연구는 Methacrylate monomer를 실크직유 속에서 중합시킴으로서 실크의 방추도를 향상시킬 목적으로 진행되었으며 이 목적을 달성하기 위하여 다음 몇가지 시료직물을 원포와 가공포로 분류하고 세탁을 반복함에 따른 방추도, 강연도 및 세탁수축도를 조사하였다. (1)Polyester, Geogette, 직물밀도…90cm-85g/m (2)Silk, Twill, 정사견, 박지, 직물밀도…90cm-90g/m (3)Silk, Twill, 정사견, 후지, 직물밀도…90cm-200g/m (4)Silk, Satin, 정사견, 박지, 직물밀도…90cm-90g/m 얻어진 결과를 종합하면 다음과 같다. (1)가공처리한 견직물들의 방추도는 원포의 것보다 약 10%의 증가를 보였다. (2)박지견직물의 방추도가 만족할 만치 개선되었으나 후지견직물은 다소 미흡한 결과이였다. (3)강연도는 가공견직물들의 촉감이 손상되지 않는 범위에서 가공된 사실을 확인하기 위하여 한 것인바 문제점이 없었다. (4)세탁후의 수축도는 모든 견직물이 polyester 보다 크게 나왔는데 그 이유는 견직물의 공장정리공정에 tenter처리로 물리적 증폭된 것을 원포로 썼기 때문으로 본다. (5)각 직물의 방추도, 강연도 및 방추도가 세탁반복에 따라 다소간 나쁜 방향으로 변하고 있는 결과를 보았는데 이것은 직유의 취화처리에도 원인이 있다고 본다. (6)결론적으로 견직물을 수지가공했다고 세탁해서 착용할 것이 아니라 역시 dry deaning을 하여 가공효과를 유지하는 것이 상책으로 본다.