Abstract
A new class of polyhydrazones has been synthesized by the solution polycondensation from equimolecular amounts of aromatic dialdehydes such as para, meta, ortho-phthal aldehyde, 5,5'-methylene-bis-salicyl aldehyde (PPTA, MPTA, OPTA, MBSA) and dihydrazides, 5,5'-methylene-bis-salicylic dihydrazide (MBSDH), terephthalic dihydrazide (TDH), sebacic dihydrazide (SDH) in DMF-$CH_3COOH$ solution. The solubility characteristics, spectral, and thermal properties of the synthesized polyhydrazones and their metal chelates were also studied. These polyhydrazones and their metal chelates except the polyhydrazone prepared from OPTA-MBSDH were generally insoluble in common organic solvents. The thermogravimetric analysis of polyhydrazones showed 10% weight losses at 250∼350$^{\circ}$C and residual weight at 500$^{\circ}$C were 32.5∼62.5%. The decomposition temperature of higher relatively, and the metal chelates decrease in the following orders; Zn(II)-IIa > Ni(II)-IIa > Co(II)-IIa > Cu(II)-IIa.
$p^-$, $m^-$, o-phthalaldehyde 및 5,5'-methylene-bis-salicyl aldehyde (PPTA, MPTA, OPTA, MBSA)와 5,5'-methylene-bis-salicylic dihydrazide, terephthalic dihydrazide 및 sebacic dihydrazide(MBSDH, TDH 및 SDH)등의 디히드라지드 화합물을 DMF-$CH_3COOH$ 혼합용액 중에서 축합반응으로 몇가지 새로운 폴리히드라존을 합성하였다. 합성한 폴리히드라존과 그의 금속킬레이트의 용해성, 흡수스펙트라 및 열적성질에 대하여 검토하였다. OPTA와 MBSDH의 반응으로 얻어진 폴리히드라존을 제외한 폴리히드라존과 그의 금속킬레이트는 일반적으로 보통 유기용매에 불응성이었다. 폴리히드라존의 중량열분석 결과 250-350$^{\circ}$C 사이에서 10%의 중량감소가 일어났고 500$^{\circ}$C고 500 폴리히드라존의 중량열분석 결과 250~350$^{\circ}$C 사이에서 10%의 중량감소가 일어났고 500$^{\circ}$C에서 32.5~63.5% 범위의 잔유중량을 나타내었다. 합성한 폴리히드라존 중에서 PPTA-MBSDH(IIa)및 MBSA-MBSDH(IIIa)가 열분해온도가 비교적 높았으며 IIa의 금속킬레이트에 있어서는 Zn(II)-IIa>Ni(II)-IIa>Co(II)-IIa>Cu(II)-IIa의 순서로 열분해온도가 저하되었다.