국산주물사(國産鑄物砂)의 입도분포(粒度分布)와 입형(粒形)에 따른 상온성질(常溫性質)에 관(關)한 연구(硏究)

A Study on the Room Temperature Properties of Domestic Molding Sand depending on the Variations of Sand Grain Distribution and Grain Shape.

Green compressive strength, permeability, deformation, flowability, compactability and green hardness values at room temperature are dependable on the grain distribution and grain shape. The results obtained under constant moisture (4% for sand) and bentonite (8% for sand) were as follows; 1. With decreasing grain size, surface area of sand grain was increased. 2. With decreasing grain size, coefficient of angularity was increased. 3. As surface area increased from $8926.43cm^2$ to $21211.16cm^2$ , green compressive strength was increased from $210.93\;g/cm^2$ to $449.98\;g/cm^2$, hardness was increased from 76.7 to 82.3, but permeability was decreased from $411.7\;{\frac{\;cc\;{\cdot}\;cm\;}{atm\;{\cdot}\;cm^2\;{\cdot}\;min.}}$ to $113.7\;{\frac{\;cc\;{\cdot}\;mm\;}{atm\;{\cdot}\;cm^2\;{\cdot}\;min.}}$ 4. As surface area increased from $8926.43\;cm^2$ to $21211.16\;cm^2$, flowability was decreased from 82.3% to 80.8%, deformation was decreased from $67.1\;cm\;{\times}\;10^{-3}$ to $54.6\;cm\;{\times}\;10^{-3}$, but compactability was increased from 44.8% to 54.3%. 5. Room temperature properties of molding sand were affected by variation of surface area.