고성능유동화제가 콘크리트의 공학적 특성에 미치는 영향 (I)

A Study on the Effects of Superplasticizers on the Engineering Preperties of Plain Concrete (I)

This study was attempted in order to investigate the effects of superplasticizers on fresh and hardened concrete. The experimental program included tests on the slump and slump loss, bleeding, time of set, air content, the compacting, factor Vee Dee, compressive strength, tensile and flexural strength, permeability, shrinkage and freege-thaw durability. The major conclusions that can be drawn on the study are as follows. 1. Superplasticizers were observed to have an appreciable fluidifying action in fresh concrete so that tinder appropriate conditions, they either considerably improved its workability or permitted a water reduction of at least 8-12% to be made while maintaining normal workability. 2. The bleeding ratios of base and S,P. Concrete were much lower than those of the conventional concrete. Differences between the base and S.P. Concrete were insignifician. 3. The setting time was the longest for conventionla concrete, followed by S.P. concrete and base concrete in thatorder. And AE water reduction admixtures showed an appreciable influence on the setting and hardening characteristics of concrete and prolonged the stiffening times. 4. The high initial slump values of S.P. concrete generally decreased rapidly with increased standing time. CF values showed increasing tendencies with the increase of S.P. content, and excessive addition of S.P. caused the segregation of fresh concrete, resulting in its rejection. 5. Though there was a slight increase in strength, no significant differences are observed between base and S.P. concrete in terms of the compressive, tensile and flexural strength. 6. The permeability of S.P. concrete was significantly less than that of the conventional concrete, and the shrinkage of S.P. concrete was considerably smaller than that of the conventional concrete, but there were no significant differences between base and S.P. concrete. 7. Compared to base concrete, S.P. concrete without entrained air tended to slightly increase freeze-thaw durability, and S.P. concrete with an appropriate entrained air gave satisfactory resistance to freezing and thawing.