Determination of Constant Friction Factor and Forming Characteristics of Sintered Porous Metal

소결금속 의 성형 특성 및 마찰 상수 결정 에 관한 연구

On the basis of plasticity theory for porous metal, an analysis of ring compression is carried out, employing the upper bound approach. The plastic flowability and the neutral radius of porous metal ring are calculated and deformation characteristics of power forging are obtained from this result. The experiments on ring compression are carried out for sintered iron porous metal with various relative densities under various friction conditions. A good agreement is observed between the shapes of the calculated curves and the experimental results from the ring compression test. The friction factor for powder metal forming can be determined not only from the relationship between reduction in height and reduction in internal diameter but independently from the relationship between reduction in height and relative density, if the initial relative density is known.

본 연구에서는 상계해 이론으로부터 마찰 상수 m에 대한 해석을 시도하여 조 직의 치밀화, 링의 내경감소율 등의 소결금속에 대한 성형특성을 여러가지 상대밀도, 마찰상수에 대해서 계산했다. 실험은 철 분말 소결금속인 시편을 상대밀도가 0.75, 0.85, 0.9이고 링의 외경:내경:높이의 비가 6:3:1과 6:3.1:1.5로 제작했고, 평 금형 (parallel platens) 사이에서 여러가지 윤활상태로 시행하여 그 실험치와 이론치들을 비교 하였다.