A Study on Cast Structure and Mechanical Properties of Al-10% Mg Alloy Solidified Under High Hydraulic Pressure

고압주조한 Al-10% Mg 합금의 주조조직 및 기계적 성질에 관한 연구

In order to study the cast structure and mechanical properties of Al-10 % Mg alloy solidified under the various high hydraulic pressure, ranging from $0kgf/cm^2$ to $2000㎏f/cm^2$ , the relationship between the cooling rate and the cast structure was observed, and also the mechanical test and the measurement of the specific gravity were carried out. From this experiment, results were summerized as follows; 1. The cooling rate of the alloy increased with increase of the applied pressure. 2. The formation of the piping and the porosity in the castings was surpressed by applying the high hydraulic pressure. 3. The dendrite arm spacing decreased with increase of the applied pressure. 4. Mechanical properties and specific gravity increased with the increase of the applied pressure.

본 실험에서는 고정수압하에서 응고한 Al-l0% Mg합금의 조직 및 기계적 성질에 미치는 가압력의 영향을 조사하기 위하여 압력을 $0㎏f/cm^2$, 500$kgf/cm^2$, $1500㎏f/cm^2$ 및 $2000㎏f/cm^2$로 변화시키면서 냉각곡선, 조직검사, 기계적시험 및 비중 측정을 하여 얻은 결론은 다음과 같다. 1. 가압력이 증가할수록 합금의 냉각속도는 증가하였다. 2. 기공 및 수축공의 발생은 가압에 의해 억제되었다. 3. 가압력이 증가할수록 dendrite arm spacing은 감소하였다. 4. 기계적 성질 및 비중은 가압력이 증가함에 따라 증가하였다.